4.1 The test method measures the degree to which the sharp corners are covered by different coating powder materials. Corner coverage is affected by surface thickness, thixotropy, melt viscosity, surface tension, curing rate, and application and curing temperature.

نطاق
1.1 The test method consists of determining the ratio of angular thickness (يرى 3.1.3) to face thickness (يرى 3.1.4) of a powder coating applied to a specific face thickness by immersing a preheated square rod in an aerated powder and curing the coating with predetermined conditions.

أستم د 2967-2017 “طلاء الزاوية لطلاءات المسحوق”

ملحوظة 1: The property of corner coverage is also known as “edge coverage”, but the latter is not recommended. There are widespread misconceptions and expectations about the term “edge coverage”. The test was performed on rebar with square angles and the results are not necessarily associated with sharper edges, namely burrs. Coatings with measurable corner coverage may still not protect sharper edges from corrosion or provide the electrical insulation required for some applications.

1.2 تعتبر القيم المعبر عنها بوحدات النظام الدولي (SI) بمثابة معايير. القيم الواردة بين قوسين هي للإشارة فقط.

1.3 ليس المقصود من هذا المعيار معالجة جميع قضايا السلامة, لو اي, المرتبطة باستخدامه. تقع على عاتق مستخدمي هذا المعيار مسؤولية إنشاء ممارسات السلامة والصحة المناسبة وتحديد إمكانية تطبيق القيود التنظيمية قبل الاستخدام..

1.4 تم تطوير هذه المواصفة القياسية الدولية وفقًا لمبادئ التقييس المعترف بها دوليًا المنصوص عليها في القرار الخاص بمبادئ تطوير المعايير الدولية, المبادئ التوجيهية والتوصيات الصادرة عن لجنة الحواجز الفنية أمام التجارة التابعة لمنظمة التجارة العالمية.