משמעות ושימוש
4.1 This test method measures the extent to which different coating powder materials cover sharp corners. Corner coverage is affected by surface thickness, thixotropy, melt viscosity, מתח פנים, curing rate, and application and curing temperature.

טווח
1.1 The test method consists of determining the ratio of angular thickness (לִרְאוֹת 3.1.3) to surface thickness (לִרְאוֹת 3.1.4) of the powder coating applied to a particular surface thickness by dipping a preheated square rod into an aerated powder and curing the coating using predetermined conditions.

הערה 1: The corner cover property is also called “edge cover”, but the latter is not recommended. There are widespread misconceptions and expectations about the term “edge coverage”. The test was performed on steel bars with square corners, and the results do not necessarily correlate with sharper edges, i.e., burrs. Coatings with measurable corner coverage may still not protect sharper edges from corrosion or provide the electrical insulation required for some applications.

1.2 Values expressed in SI units shall be regarded as standard. הערכים המופיעים בסוגריים הם לעיון בלבד.

1.3 תקן זה לא נועד להתייחס לכולם, אם בכלל, חששות בטיחות הקשורים לשימוש בו. באחריות המשתמשים בתקן זה לקבוע נוהלי בטיחות ובריאות מתאימות ולקבוע את תחולת ההגבלות הרגולטוריות לפני השימוש.

1.4 תקן בינלאומי זה מבוסס על עקרונות התקינה המוכרים בעולם שנקבעו בהחלטה על עקרונות לפיתוח תקנים בינלאומיים, הנחיות והמלצות שהונפקו על ידי ועדת ה-WTO בנושא חסמים טכניים לסחר.