Arti dan Tujuan
3.1 Metode pengujian ini dapat digunakan untuk menentukan berbagai tahapan dan kecepatan pengeringan, curing and film formation of organic coatings to compare coating types, to assess the effect of compositional changes on drying times, or to assess drying/curing times on the shop floor or in the field. Low temperatures can significantly slow down the drying rate of coatings, so it is often possible to use low-temperature curing agents, katalis, and/or accelerators to aid in drying and film formation at cooler temperatures. Method B aims to assess these components and/or determine the effect of lower temperatures on drying rates. sebaliknya, the drying/curing rate of some coatings is accelerated under high temperature/humidity conditions, while others may be adversely affected by elevated humidity. Method C was designed to evaluate the effect of high temperature and relative humidity conditions on drying, curing and film formation of paints and coatings. The terms dry or dry, cured or cured, and film forming are used interchangeably throughout the standard.

3.2 Test Methods A, B and C are limited to comparing paints/coatings applied to smooth, non-absorptive substrates and do not reflect the effect of paint carrier absorption into substrates.

ASTM D 1640-2022: Pengeringan, Pengobatan, dan Pembentukan Film Lapisan Organik pada Suhu Kamar

Ruang lingkup
1.1 These test methods cover the various stages and rates of film formation during drying or curing of organic coatings under laboratory controlled air temperature (rendah, ambient and/or elevated) and/or humidity conditions. Procedures for assessing drying under prevailing conditions of workshop and field temperature and humidity are also described.

1.2 Values expressed in SI units or ink-pound units should be treated separately as standard values. Nilai yang ditentukan pada setiap sistem belum tentu sama; Karena itu, untuk memastikan kepatuhan terhadap standar, setiap sistem harus digunakan secara independen satu sama lain dan nilai-nilai dari kedua sistem tidak boleh digabungkan.

ASTM D 1640-2022: Pengeringan, Pengobatan, dan Pembentukan Film Lapisan Organik pada Suhu Kamar

1.3 Standar ini tidak dimaksudkan untuk mengatasi semua masalah keselamatan, jika ada, terkait dengan penggunaannya. Pengguna standar ini bertanggung jawab untuk menetapkan keselamatan yang sesuai, praktik kesehatan dan lingkungan dan untuk menentukan penerapan pembatasan peraturan sebelum digunakan.

1.4 Standar internasional ini telah dikembangkan sesuai dengan prinsip-prinsip standardisasi yang diakui secara internasional yang ditetapkan dalam Keputusan Prinsip-Prinsip Pengembangan Standar Internasional, Pedoman dan Rekomendasi yang dikeluarkan oleh Komite Hambatan Teknis Perdagangan Organisasi Perdagangan Dunia.