Arti dan Tujuan
5.1 Korosi eksternal pada logam yang dicat dipengaruhi oleh banyak faktor, termasuk: suasana korosif, hujan, embun yang mengembun, ultraviolet light, wet/dry cycle and temperature cycle. These factors often have synergistic effects on each other. This practice is intended to provide a more realistic simulation of the interaction of these factors than conventional testing with continuous exposure to a set of static corrosion conditions.

5.2 The results obtained from this exercise can be used to compare the relative durability of materials subjected to a particular test cycle.

5.3 No exposure test can be specified as a complete simulation of actual conditions of use in outdoor environments. Only when a rank correlation has been established for the particular material being tested can the results obtained from the exposure performed according to this practice be considered representative of the actual outdoor exposure. The relative durability of materials in actual outdoor service can vary considerably from location to location due to differences in UV radiation, waktu basah, suhu, kontaminan, dan faktor lainnya. Dengan demikian, even if results from specific artificial test conditions are found to be useful for comparing the relative durability of materials exposed to specific external environments, it cannot be assumed that they can be used to determine the relative durability in different environments.

5.4 Although very tempting, it is not recommended to calculate an “acceleration factor” that relates x hours of laboratory exposure to y months of external exposure. Different materials and different formulations of the same material may have significantly different acceleration coefficients. The acceleration factor also varies according to changes in degradation rates in laboratory tests and actual outdoor exposures.

5.5 This practice is suitable for comparing the relative performance of materials tested simultaneously in the same exposure device. Since there may be differences between the same type of exposure equipment, it is not recommended to compare the amount of degradation in different equipment exposed to the same duration of material at different times or running the same test conditions. This practice should not be used to establish “pass/fail” approvals for materials after a specific exposure period unless performance is compared relative to control materials exposed at the same time or variability in testing is rigorously quantified so that statistically significant pass/fail judgments can be made.

5.6 This practice has been found to be useful for air-dried industrial maintenance coatings on steel 3,4,5,6,7 and zinc-rich primers, but its applicability in high UV stability coating systems, such as automotive applications, has not been evaluated.

ASTM D 5894-2021 “Semprotan Garam Siklik/Paparan UV pada Logam yang Dicat (atau Paparan pada Ruang Semprotan Garam/Pengeringan dan Ruang UV/Kondensor)”

Ruang lingkup
1.1 The practice covers the fundamentals and operational practices of cyclic corrosion/UV exposure of paint on metal, with alternate exposure in two different cabinets: a cyclic salt spray/drying cabinet and a fluorescent UV/condensing cabinet.

1.2 This practice is limited to methods and procedures for obtaining, measuring and controlling exposure conditions. It does not specify the preparation of the specimens or the evaluation of the results.

1.3 Nilai yang dinyatakan dalam satuan SI harus dianggap sebagai nilai standar. Satuan pengukuran lain tidak termasuk dalam standar ini.

1.4 Standar ini tidak dimaksudkan untuk mengatasi semua masalah keselamatan, jika ada, terkait dengan penggunaannya. Pengguna standar ini bertanggung jawab untuk menetapkan keselamatan yang sesuai, praktik kesehatan dan lingkungan dan untuk menentukan penerapan pembatasan peraturan sebelum digunakan.

1.5 Standar internasional ini telah dikembangkan sesuai dengan prinsip-prinsip standardisasi yang diakui secara internasional yang ditetapkan dalam Keputusan Prinsip-Prinsip Pengembangan Standar Internasional, Pedoman dan Rekomendasi yang dikeluarkan oleh Komite Hambatan Teknis Perdagangan Organisasi Perdagangan Dunia.