意味と目的
4.1 鏡面光沢度は、主にフィルムや表面の光沢の外観を測定するために使用されます。. A precise comparison of gloss values is meaningful only if the same measurement procedure and the same general material type are involved. 特に, the gloss values of transparent films should not be compared with those of opaque films and vice versa. Glossiness is a complex property of surfaces that cannot be measured entirely by any single number.

4.2 Specular gloss usually varies with surface smoothness and flatness. It is sometimes used for comparative measurements of these surface properties.

ASTM D 2457-2021 プラスチックフィルムおよび固体プラスチックの鏡面光沢度の標準試験方法

の範囲
1.1 The test method describes procedures for measuring the glossiness of opaque and transparent plastic films and solid plastics. It contains four independent gloss angles (注記 1) :

1.1.160 度, recommended for medium light films,

1.1.220 度, recommended for high light film,

1.1.345 度, recommended for medium and low light films,

1.1.485 度, recommended for medium and low gloss films, 同じように

1.1.575 度, recommended for plastic siding and soffit.

注記 1: The measuring devices and methods of 85 度, 75 度, 60 degrees and 20 degrees are repeated with those in test methods D523 and D3679; The equipment and methods for the 45° procedure were also taken from test method C346.

1.2 この規格は、すべての安全問題に対処することを目的としたものではありません, もしあれば, その使用に関連する. 適切な安全性を確立するのは、この規格の使用者の責任です。, 健康および環境慣行を確認し、使用前に規制制限の適用可能性を判断するため.

ASTM D 2457-2021 プラスチックフィルムおよび固体プラスチックの鏡面光沢度の標準試験方法

注記 2: There is no known ISO equivalent to this standard.

1.3 この国際規格は、国際規格開発の原則に関する決定で確立された国際的に認められた標準化原則に従って開発されました。, 世界貿易機関の貿易の技術的障壁に関する委員会が発行したガイドラインと勧告.