의미와 목적
5.1 The test method can be used to select coating powders with similar melt flow characteristics at minimum shear forces. It is not recommended to use it as an absolute measure, but as a comparative measure for samples measured simultaneously on the same panel.

범위
1.1 This test method specifies a method for determining the flow characteristics of a molten thermoset paint powder along a plane inclined in a horizontal direction. This test indicates the degree of melt flow that may occur during the curing of the paint powder. This property contributes to coating coherence, surface appearance and coverage of sharp edges (see test method D2967), 하지만, it should not be used as a factor in judgment. This test is a useful way to check for batch-to-batch variation in the behavior of a given paint powder. There was no correlation between the results for the different composition of paint powders. This method is unlikely to yield meaningful results for paint powders with a gel time of less than one minute at the test temperature (see test method D4217). Oven ventilation, tilt Angle, and particle variation can significantly affect the results, making inter-laboratory reproducibility difficult to correlate.

ASTM D 4242-2017 “열경화성 분말 코팅의 틸팅 플레이트 유동성”

1.2 SI 단위로 표현된 값은 표준으로 간주됩니다.. 괄호 안의 값은 참고용입니다..

1.3 이 표준은 모든 안전 문제를 다루기 위한 것이 아닙니다., 만약에 어떠한, 그 사용과 관련된. 적절한 안전 및 보건 관행을 확립하고 사용 전에 규제 제한의 적용 가능성을 결정하는 것은 이 표준 사용자의 책임입니다..

1.4 본 국제 표준은 국제 표준 개발 원칙에 관한 결정에서 확립된 국제적으로 인정받는 표준화 원칙에 따라 개발되었습니다., 세계무역기구(WTO) 무역기술장벽위원회가 발행한 지침 및 권고사항.