JIS K6259-2004 “가황고무와 열가소성 고무의 내오존성 측정”
JIS K6259 standard introduction
JIS K6259 is a test method for “가황고무와 열가소성 고무의 내오존성 측정”. The following is part of the original English standard. For copyright protection, if you need the full text of JIS K6259 standard or the Chinese version of JIS K6259 standard, please contact customer service.
1 범위
This Japanese Industrial Standard specifies the testing methods t o measure the resistance to ozone cracking for vulcanized rubber.
Remarks 1 The standards cited in this Standard are listed as follows:
JIS K 6200 Glossary of terms used in rubber industry
JIS K 6250 General rules of physical testing methods for rubber,가황 또는 열가소성
JIS K 6251 Tensile testing methods for vulcanized rubber
JIS K 8001 General rule for test methods of reagents
JIS K 8637 Sodium thiosulfate pentahydrate
JIS K 8913 Potassium iodide
JIS K 9007 Potassium dihydrogenphosphate
JIS K 9019 Disodium hydrogenphosphate 12-water
JIS K6259-2004 “가황고무와 열가소성 고무의 내오존성 측정”
2 The International Standards corresponding to this Standard are listed as follows:
IS0 1431-1:1989 고무, 가황 또는 열가소성 – 오존 균열에 대한 저항성 – 부분 1 :Static strain test
ISOIDIS 1431-2:1992 고무, 가황된 – 오존 균열에 대한 저항성 – 부분 2 :Dynamic strain test
3 The units and numerical values given in ( 1 in this Standard are based on the traditional units, and are standard values. 하지만,traditional units becomes an informative reference on and afterApril Ist, 1995.
JIS K6259-2004 “가황고무와 열가소성 고무의 내오존성 측정”
2 Definitions
For the purposes of this Standard, the definitions given in JIS K 6200 and the following definitions apply.
(1)critical strain The maximum tensile strain, which has no cracking, given when test piece has been exposed in specified ozone-concentrated atmosphere at specified temperature for specified duration.
(2)limiting strain The maximum tensile strain given when the duration needed for cracking on a test piece is very long, and when the occurring time of its cracking cannot be forecasted.
(3)정적 오존 균열 시험 시험편, 정적 인장 변형 하에서,인공적으로 제조된 저농도 오존을 함유한 공기 중에 노출되어 있는 경우,균열상태를 평가하는 시험, 균열을 만드는 데 필요한 기간, 또는 균열이 발생하지 않는 최대 인장 변형률.
(4)동적 오존 균열 시험 시험편에 동적 인장 변형을 가한 상태에서 인공적으로 제조한 저농도 오존이 함유된 공기 중에 시험편을 노출시키는 시험, 균열의 상태와 균열이 발생하는 기간을 평가하는 시험