Betekenis en gebruik
4.1 This test method measures the extent to which different coating powder materials cover sharp corners. Corner coverage is affected by surface thickness, thixotropy, melt viscosity, surface tension, curing rate, and application and curing temperature.

bereik
1.1 The test method consists of determining the ratio of angular thickness (zien 3.1.3) to surface thickness (zien 3.1.4) of the powder coating applied to a particular surface thickness by dipping a preheated square rod into an aerated powder and curing the coating using predetermined conditions.

Opmerking 1: The corner cover property is also called “edge cover”, but the latter is not recommended. There are widespread misconceptions and expectations about the term “edge coverage”. The test was performed on steel bars with square corners, and the results do not necessarily correlate with sharper edges, d.w.z., burrs. Coatings with measurable corner coverage may still not protect sharper edges from corrosion or provide the electrical insulation required for some applications.

1.2 Waarden uitgedrukt in SI-eenheden worden als standaard beschouwd. De waarden tussen haakjes zijn alleen ter referentie.

1.3 Deze standaard is niet bedoeld om iedereen te behandelen, indien aanwezig, veiligheidsproblemen die verband houden met het gebruik ervan. Het is de verantwoordelijkheid van gebruikers van deze norm om passende veiligheids- en gezondheidspraktijken vast te stellen en voorafgaand aan gebruik de toepasbaarheid van wettelijke beperkingen te bepalen..

1.4 Deze internationale norm is gebaseerd op de internationaal erkende standaardisatieprincipes die zijn vastgelegd in het Besluit over de beginselen voor de ontwikkeling van internationale normen, Richtlijnen en aanbevelingen uitgegeven door het WTO-comité voor technische handelsbelemmeringen.