JIS K6259 standard introduction
JIS K6259 is a test method for “Bepaling van de ozonbestendigheid van gevulkaniseerd rubber en thermoplastisch rubber”. The following is part of the original English standard. For copyright protection, if you need the full text of JIS K6259 standard or the Chinese version of JIS K6259 standard, please contact customer service.

1 Domein
This Japanese Industrial Standard specifies the testing methods t o measure the resistance to ozone cracking for vulcanized rubber.

Remarks 1 The standards cited in this Standard are listed as follows:

JIS K 6200 Glossary of terms used in rubber industry

JIS K 6250 General rules of physical testing methods for rubber,vulcanized or thermoplastic

JIS K 6251 Tensile testing methods for vulcanized rubber

JIS K 8001 General rule for test methods of reagents

JIS K 8637 Sodium thiosulfate pentahydrate

JIS K 8913 Potassium iodide

JIS K 9007 Potassium dihydrogenphosphate

JIS K 9019 Disodium hydrogenphosphate 12-water

JIS K6259-2004 “Bepaling van de ozonbestendigheid van gevulkaniseerd rubber en thermoplastisch rubber”

2 The International Standards corresponding to this Standard are listed as follows:

IS0 1431-1:1989 Rubber, vulcanized or thermoplastic – Resistance to ozone cracking – Deel 1 :Static strain test

ISOIDIS 1431-2:1992 Rubber, vulcanized – Resistance to ozone cracking – Deel 2 :Dynamic strain test

3 The units and numerical values given in ( 1 in this Standard are based on the traditional units, and are standard values. Echter,traditional units becomes an informative reference on and afterApril Ist, 1995.

JIS K6259-2004 “Bepaling van de ozonbestendigheid van gevulkaniseerd rubber en thermoplastisch rubber”

2 Definitions
For the purposes of this Standard, the definitions given in JIS K 6200 and the following definitions apply.

(1)critical strain The maximum tensile strain, which has no cracking, given when test piece has been exposed in specified ozone-concentrated atmosphere at specified temperature for specified duration.

(2)limiting strain The maximum tensile strain given when the duration needed for cracking on a test piece is very long, en wanneer het tijdstip van barsten niet kan worden voorspeld.

(3)statische ozon-kraaktest Bij een proefstuk, onder een statische trekbelasting,wordt blootgesteld aan de lucht die kunstmatig bereid laaggeconcentreerd ozon bevat,de test om de toestand van scheurvorming te evalueren, de duur die nodig is om scheuren te maken, of de maximale trekspanning waarbij geen scheuren optreden.

(4)dynamische ozonscheurtest Wanneer een proefstuk wordt blootgesteld aan de lucht die kunstmatig bereid laaggeconcentreerd ozon bevat, terwijl er dynamische trekspanning op het proefstuk wordt uitgeoefend, de test om de toestand van het scheuren te beoordelen en de duur waarmee het scheuren plaatsvindt