Significado e uso
4.1 Materiais feitos de plásticos fotodegradáveis ​​deterioram-se rapidamente quando expostos à radiação solar, oxigênio, aquecer, moisture and other weather-degrading elements. This practice is used to assess the photodegradability of plastics when exposed to devices that produce simulated daylight (1,2) 6 and control temperature and humidity. The exposures used in this practice are not intended to simulate deterioration caused by local weather phenomena such as atmospheric pollution, ataques biológicos, e exposição à água salgada. Positive correlation of exposure results between this device and other laboratory aging devices is not possible.

4.2 Changes in results can be expected when operating conditions vary within the accepted limits of this practice. Portanto, all test results using this specification need to be accompanied by the specific operating conditions required in Section 9. For more information about the precautions that apply to using results obtained under this practice, see Practice G151.

4.3 The results of laboratory exposure cannot be directly extrapolated to estimate the absolute rate of environmental degradation, as the acceleration factor depends on the material and can vary greatly for each material and different formulations of the same material. No entanto, exposure to similar materials with known outdoor properties, controles, and simultaneously with test samples allows comparison of durability under test conditions relative to controls. The evaluation of relative durability also greatly improves the consistency of test results between different laboratories (3).

4.4 Test results will depend on the degree of care taken to operate the equipment in accordance with practice G155. Fatores importantes incluem regulação da tensão da linha, ausência de sal ou outros depósitos de água, controle de temperatura e umidade, and condition and age of burners and filters.

Observação 2: Para obter informações adicionais sobre fontes de variabilidade e estratégias para lidar com a variabilidade no projeto, execução, e análise de dados de ensaios laboratoriais de exposição acelerada, see Guideline G141.

4.5 Before continuing this practice, it is common practice to refer to the specifications of the material under test. Any sample preparation, ajustamento, sizing, or test parameter or combination thereof covered in the Material Specification shall take precedence over the sample preparation, ajustamento, sizing, or test parameter or combination thereof referred to in this specification. If there is no material specification, default conditions apply.

Método de teste padrão ASTM D5071-2022 para teste de exposição de plásticos fotodegradáveis ​​em dispositivos com lâmpada de xenônio:

Raio
1.1 This procedure covers specific procedures and test conditions applicable to xenon arc exposure of photodegradable plastics in accordance with practices G151 and G155. The practice also includes the preparation of samples, suitable test conditions for photodegradable plastics, e avaliação dos resultados dos testes.

1.2 Esta norma não se destina a abordar todas as questões de segurança, caso existam, associado ao seu uso. É responsabilidade dos usuários desta norma estabelecer medidas de segurança apropriadas, práticas de saúde e ambientais e para determinar a aplicabilidade de restrições regulatórias antes do uso.

Observação 1: This practice is technically equivalent to ISO 4892-2 and Practice D2565, which covers xenon arc exposure of long-term plastics for outdoor applications.

1.3 Esta norma internacional é baseada em princípios de padronização reconhecidos internacionalmente, estabelecidos na Decisão sobre Princípios para o Desenvolvimento de Normas Internacionais, Diretrizes e recomendações emitidas pelo Comitê da OMC sobre Barreiras Técnicas ao Comércio.