ความหมายและการใช้งาน
4.1 วิธีทดสอบนี้จะวัดขอบเขตที่วัสดุผงเคลือบต่างๆ ครอบคลุมมุมที่แหลมคม. Corner coverage is affected by surface thickness, thixotropy, melt viscosity, surface tension, curing rate, and application and curing temperature.

พิสัย
1.1 The test method consists of determining the ratio of angular thickness (ดู 3.1.3) to surface thickness (ดู 3.1.4) of the powder coating applied to a particular surface thickness by dipping a preheated square rod into an aerated powder and curing the coating using predetermined conditions.

บันทึก 1: The corner cover property is also called “edge cover”, but the latter is not recommended. There are widespread misconceptions and expectations about the term “edge coverage”. The test was performed on steel bars with square corners, and the results do not necessarily correlate with sharper edges, เช่น., burrs. Coatings with measurable corner coverage may still not protect sharper edges from corrosion or provide the electrical insulation required for some applications.

1.2 Values expressed in SI units shall be regarded as standard. ค่าที่ระบุในวงเล็บมีไว้เพื่อการอ้างอิงเท่านั้น.

1.3 มาตรฐานนี้ไม่ได้มุ่งหมายที่จะกล่าวถึงทั้งหมด, ถ้ามี, ข้อกังวลด้านความปลอดภัยที่เกี่ยวข้องกับการใช้งาน. เป็นความรับผิดชอบของผู้ใช้มาตรฐานนี้ในการกำหนดแนวทางปฏิบัติด้านความปลอดภัยและสุขภาพที่เหมาะสม และเพื่อพิจารณาการบังคับใช้ข้อจำกัดด้านกฎระเบียบก่อนใช้งาน.

1.4 มาตรฐานสากลนี้ตั้งอยู่บนหลักการมาตรฐานที่ได้รับการยอมรับในระดับสากลซึ่งกำหนดไว้ในการตัดสินใจเกี่ยวกับหลักการเพื่อการพัฒนามาตรฐานสากล, แนวทางและข้อเสนอแนะที่ออกโดยคณะกรรมการ WTO ว่าด้วยอุปสรรคทางเทคนิคต่อการค้า.