4.1 The test method measures the degree to which the sharp corners are covered by different coating powder materials. Corner coverage is affected by surface thickness, thixotropy, melt viscosity, surface tension, curing rate, and application and curing temperature.

Kapsamı
1.1 The test method consists of determining the ratio of angular thickness (Görmek 3.1.3) to face thickness (Görmek 3.1.4) of a powder coating applied to a specific face thickness by immersing a preheated square rod in an aerated powder and curing the coating with predetermined conditions.

ASTM D 2967-2017 “Toz Boyaların Köşe Kaplaması”

Not 1: The property of corner coverage is also known as “edge coverage”, but the latter is not recommended. There are widespread misconceptions and expectations about the term “edge coverage”. The test was performed on rebar with square angles and the results are not necessarily associated with sharper edges, namely burrs. Coatings with measurable corner coverage may still not protect sharper edges from corrosion or provide the electrical insulation required for some applications.

1.2 SI birimlerinde ifade edilen değerler standart olarak kabul edilecektir.. Parantez içinde verilen değerler yalnızca referans amaçlıdır.

1.3 Bu standardın tüm güvenlik konularını ele alması amaçlanmamıştır., varsa, kullanımıyla ilgili. Uygun güvenlik ve sağlık uygulamalarını oluşturmak ve kullanımdan önce düzenleyici kısıtlamaların uygulanabilirliğini belirlemek bu standardı kullananların sorumluluğundadır..

1.4 Bu uluslararası Standart, Uluslararası Standartların Geliştirilmesine İlişkin İlkeler Kararında belirlenen uluslararası kabul görmüş standardizasyon ilkelerine uygun olarak geliştirilmiştir., Dünya Ticaret Örgütü Ticaretin Önündeki Teknik Engeller Komitesi tarafından yayımlanan Kılavuz ve Tavsiyeler.