Anlamı ve kullanımı
5.1 Cihaz numuneyi ışığa maruz bırakır, ısı ve isteğe bağlı nem, typically attempting to replicate the changes in specimen characteristics observed in both outdoor and indoor end-use environments. Maruz kalmanın amacı, atmosferik kirlilik gibi yerel hava olaylarından kaynaklanan bozulmayı simüle etmek değildir., biyolojik saldırılar, ve tuzlu suya maruz kalma.

5.2 This practice allows for a wide range of exposure conditions that may produce significantly different results. Öyleyse, the results of its use should not be referred to unless accompanied by a report in section 10 detailing specific operating conditions.

5.2.1 Controls (similar materials with known properties) should be exposed at the same time as the sample to provide a reference for comparison purposes. It is better to use two different control materials: one known to have relatively poor durability and the other known to have relatively good durability. Each sample and control material should be repeated at least three times at the same time for statistical evaluation of the results.

ASTM G155-2021 Metalik Olmayan Malzemelerin Maruz Kalmasına Yönelik Ksenon Ark Lambası Ekipmanı Uygulaması

5.3 Results obtained from specimens exposed in different devices (even if the device is of the same model) using the same set point and operational controls should not be compared unless repeatability of the material to be tested has been established between devices.

5.4 Please refer to Practice G151 for warning guidelines applicable to all laboratory aging equipment.

5.5 Users are advised to follow good laboratory practices to reduce exposure variability (1). 8

Yarıçap
1.1 This practice is limited to the basic principles and procedures for operating xenon arc lamps and water installations; Kendi kendine, spesifik sonuçlar sağlamaz.

1.2 Uygulamalar için spesifik maruz kalma koşullarını tanımlayan uygulamalar veya yöntemler ve malzeme özelliklerindeki değişiklikleri değerlendirmeye yönelik yöntemler ile birlikte kullanılması amaçlanmıştır.. This practice aims to reproduce the weathering effects that occur when materials are exposed to sunlight (directly or through window glass) ve nem (such as humidity, yağmur, or dew) during actual use. This practice is limited to procedures for obtaining, measuring, and controlling exposure conditions.

ASTM G155-2021 Metalik Olmayan Malzemelerin Maruz Kalmasına Yönelik Ksenon Ark Lambası Ekipmanı Uygulaması

Not 1: A number of exposure procedures are listed in the appendix; Fakat, this practice does not specify the appropriate exposure conditions for the material to be tested.

Not 2: Practice G151 describes the general procedures and performance requirements used when exposing materials in equipment that uses laboratory light sources.

1.3 Under controlled environmental conditions, the sample is exposed to light from an optically filtered xenon arc lamp. The combinations of different types of filters and xenon arc sources are described.

1.4 Sample preparation and result evaluation are covered in ASTM methods or specifications for specific materials. General guidance is given in Practice G151.

Not 3: General information on methods for determining post-exposure changes in properties and reporting these results is described in Practice D5870.

1.5 This practice does not apply to corrosion testing of bare metals.

1.6 Birimler – SI birimlerinde ifade edilen değerler standart değerler olarak kabul edilmelidir. Bu standartta başka hiçbir ölçü birimi yer almamaktadır..

1.7 This practice is technically similar to the following ISO documents: ISO 4892-2, ISO 16474-2, ISO 105-B02, ISO 105-B04, ISO 105-B05, ISO 105-B06 and ISO 105-B10.

ASTM G155-2021 Metalik Olmayan Malzemelerin Maruz Kalmasına Yönelik Ksenon Ark Lambası Ekipmanı Uygulaması

1.8 Bu standardın tüm güvenlik konularını ele alması amaçlanmamıştır., varsa, kullanımıyla ilgili. Uygun güvenliğin sağlanması bu standardın kullanıcılarının sorumluluğundadır., sağlık ve çevre uygulamaları ve kullanımdan önce düzenleyici kısıtlamaların uygulanabilirliğini belirlemek.

1.8.1 If the operation of the lamp produces any ozone, it should be removed from the sample and the operator through the exhaust system.

1.9 Bu uluslararası standart, Uluslararası Standartların Geliştirilmesine İlişkin İlkeler Kararında belirlenen uluslararası kabul görmüş standardizasyon ilkelerine dayanmaktadır., DTÖ Ticaretin Önündeki Teknik Engellere İlişkin Komite tarafından yayınlanan Kılavuzlar ve Tavsiyeler.