抽象的: 杯突试验是评价延展性的方法, adhesion and flexibility of a coating when the substrate is deformed. This paper introduces the scope, instrument and material of cupping test, and the measurement method and result presentation. This test is an indispensable test item for coatings that need to be post-formed in industrial manufacturing. The national standard GB/T 9753 and international standard ISO 1520 also provide relevant specifications and guidance.

1. 介绍

在涂料行业, it is very important to evaluate the performance and applicability of the coating. Cupping test is a common method used to evaluate the ductility, adhesion and flexibility of a coating when the substrate is deformed. This paper will detail the contents of the cup drawing.

2. 仪器及材料

The instruments and materials required for the cupping test are as follows:

Cup process testing machine: can be manual or hydraulic type. The key parts include a hard smooth spherical punch and a circular formwork gripper. Test process can be by binocular stereo microscope or a magnifying glass to observe.

Steel plate: thickness of 0.30~1.25mm, width and length of not less than 70mm.

Magnifying glass: 10x magnification.

杯突试验及其在涂层评价中的作用

3. The method

3.1 Preparation Before the test, the coating test plate shall be painted and dried, and the state shall be adjusted at a temperature of (23±2)°C and a relative humidity of (50±5)% for at least 16 小时.

3.2 Test procedures

The test plate is fixed between the retaining ring and the die so that the coating faces the die. Adjust the test plate so that the intersection point between the central axis of the punch and the test plate is not less than 35mm from each side of the test plate.

Open the testing machine so that the punch is pushed to the test plate at a constant speed, so that the test plate forms a dome shape with the coating facing out until the specified depth is reached or the coating cracks or separates from the substrate.

杯突试验及其在涂层评价中的作用

4. 结果表示

According to different test situations, the results can be expressed as follows:

When testing in accordance with the provisions, the stamping depth, it is after the required depth, observe whether the coating cracking or separation from the substrate, according to the evaluation standard to judge passed or not passed.

When the test is carried out at the minimum depth causing damage, the stamping depth is gradually increased to the minimum depth at which the coating begins to crack or separate from the substrate as the result.

5. 参考标准

This test method refers to the following national and international standards:

The national standard GB/T 9753 “paint and varnish cup drawing test”.

国际标准ISO 1520 “paint and varnish cup drawing test (second edition)”.

杯突试验及其在涂层评价中的作用

结论

Cupping test, as a common method for evaluating coating properties, can evaluate the ductility, adhesion and flexibility of the coating when the substrate is deformed. By performing such tests on coatings, it is possible to better understand the performance of the coating in actual use, which can guide the subsequent processing and application processes in industrial manufacturing.