Signification et utilisation
4.1 Les matériaux fabriqués à partir de plastiques photodégradables se détériorent rapidement lorsqu'ils sont exposés au rayonnement solaire, oxygène, chaleur, moisture and other weather-degrading elements. This practice is used to assess the photodegradability of plastics when exposed to devices that produce simulated daylight (1,2) 6 and control temperature and humidity. The exposures used in this practice are not intended to simulate deterioration caused by local weather phenomena such as atmospheric pollution, attaques biologiques, et exposition à l'eau salée. Positive correlation of exposure results between this device and other laboratory aging devices is not possible.

4.2 Changes in results can be expected when operating conditions vary within the accepted limits of this practice. Donc, all test results using this specification need to be accompanied by the specific operating conditions required in Section 9. Pour plus d'informations sur les précautions qui s'appliquent à l'utilisation des résultats obtenus dans le cadre de cette pratique, voir la pratique G151.

4.3 The results of laboratory exposure cannot be directly extrapolated to estimate the absolute rate of environmental degradation, as the acceleration factor depends on the material and can vary greatly for each material and different formulations of the same material. Cependant, exposure to similar materials with known outdoor properties, contrôles, and simultaneously with test samples allows comparison of durability under test conditions relative to controls. The evaluation of relative durability also greatly improves the consistency of test results between different laboratories (3).

4.4 Test results will depend on the degree of care taken to operate the equipment in accordance with practice G155. Les facteurs importants incluent la régulation de la tension de ligne, absence de sel ou d'autres dépôts d'eau, contrôle de la température et de l'humidité, and condition and age of burners and filters.

Note 2: Pour plus d’informations sur les sources de variabilité et les stratégies pour gérer la variabilité dans la conception, exécution, and data analysis of laboratory accelerated exposure trials, see Guideline G141.

4.5 Before continuing this practice, it is common practice to refer to the specifications of the material under test. Any sample preparation, adjustment, sizing, or test parameter or combination thereof covered in the Material Specification shall take precedence over the sample preparation, adjustment, sizing, or test parameter or combination thereof referred to in this specification. If there is no material specification, default conditions apply.

Méthode de test standard ASTM D5071-2022 pour les tests d'exposition des plastiques photodégradables dans les dispositifs à lampe au xénon:

Rayon
1.1 This procedure covers specific procedures and test conditions applicable to xenon arc exposure of photodegradable plastics in accordance with practices G151 and G155. The practice also includes the preparation of samples, suitable test conditions for photodegradable plastics, and evaluation of test results.

1.2 Cette norme n'est pas destinée à répondre à tous les problèmes de sécurité, si seulement, associé à son utilisation. Il est de la responsabilité des utilisateurs de cette norme d'établir des mesures de sécurité appropriées., pratiques sanitaires et environnementales et pour déterminer l’applicabilité des restrictions réglementaires avant utilisation.

Note 1: Cette pratique est techniquement équivalente à l'ISO 4892-2 and Practice D2565, which covers xenon arc exposure of long-term plastics for outdoor applications.

1.3 Cette norme internationale est basée sur les principes de normalisation internationalement reconnus établis dans la Décision sur les principes pour l'élaboration de normes internationales., Lignes directrices et recommandations émises par le Comité des obstacles techniques au commerce de l'OMC.