OIN 3233:1998 “Détermination de la fraction volumique non volatile en mesurant la densité du revêtement sec” (GB/T 9272-2007) specifies a density of dry coating obtained by measuring any specified temperature range and drying or curing time.

OIN 3233-1-2019 Nom standard: Peintures et vernis-détermination des composés non volatils en pourcentage volume – Partie 1: Method for determination of nonvolatile compounds using coated plates and for determination of dry film density according to Archimedes’ principlePractice status: current
Une préface
OIN (Organisation internationale de normalisation) est une fédération mondiale d'organismes de normalisation nationaux (Comités membres de l'ISO). L'élaboration de normes internationales est généralement réalisée par l'intermédiaire de comités techniques ISO.. Chaque groupe membre intéressé par le sujet sur lequel un comité technique a été créé a le droit d'être représenté au sein du comité.. Organisations internationales, les gouvernements et les ONG en liaison avec l’ISO sont également impliqués dans cet effort. L'ISO travaille en étroite collaboration avec la Commission électrotechnique internationale (CEI) sur toutes les questions de normalisation électrotechnique.

Partie 1 de la Directive ISO/CEI décrit les procédures utilisées pour élaborer ce document ainsi que celles utilisées pour une maintenance ultérieure.. En particulier, il convient de prêter attention aux différents critères d'approbation requis pour les différents types de documents ISO. Ce document a été rédigé conformément aux règles éditoriales de la partie 2 de la directive ISO/CEI (voir iso.org/directives).

OIN 3233-1-2019 “Peintures et vernis-détermination des composés non volatils en pourcentage volume – Partie 1: Procédé pour la détermination de composés non volatils à l'aide de plaques d'essai revêtues et pour la détermination de la densité du film sec selon le principe Akimid”

Veuillez noter que certains éléments de ce document peuvent faire l'objet de droits de brevet. L'ISO n'est pas responsable de l'identification de tout ou partie de ces droits de brevet. Les détails de tous les droits de brevet identifiés lors de l'élaboration du document figureront dans le profil et/ou dans la liste des revendications de brevet ISO reçues. (voir iso.org/patents).

Tous les noms commerciaux utilisés dans ce document sont fournis à titre d'information pour la commodité des utilisateurs et ne constituent pas une approbation de celui-ci..

Explications des normes pertinentes de volontariat, Termes spécifiques ISO liés à l'évaluation de la conformité et à l'expression de la signification, et l'ISO dans les barrières techniques au commerce (OTC) adhérer au principe de l'organisation mondiale du commerce (OMC) information, please see the iso.org/iso/foreword.html.

This document is prepared by Technical Committee ISO/TC 35, Peintures et vernis, Sous-comité SC 9, General Test methods for paints and varnishes.

La deuxième édition annule et remplace la première édition (OIN 3233-1:2013), qui a été techniquement révisé.

The main changes from the previous edition are as follows:

Definitions and sources in Chapter 3 have been updated;

— A minimum mass of 25 mg of coating on the plate is added in 7.4.1 because measurements and simulation calculations indicate that the minimum mass of coating on the plate is required;

– The text has been edited and changed.

A list of all parts in the ISO 3233 la série peut être consultée sur le site Web de l'ISO.

Any feedback or questions on this document should be directed to the user’s national standards body. A full list of these agencies can be found at iso.org/members.html.

OIN 3233-1-2019 “Peintures et vernis-détermination des composés non volatils en pourcentage volume – Partie 1: Procédé pour la détermination de composés non volatils à l'aide de plaques d'essai revêtues et pour la détermination de la densité du film sec selon le principe Akimid”

Introduction
This method is used to measure the density and determine the volume of dry coating obtained from a given volume of liquid coating. This volume is considered a very meaningful measure of the coverage of paints, vernis, or related products (the surface area covered per unit volume specified by the thickness of dry film). The values obtained by this method may differ from those calculated based on the addition of the mass and volume of the raw materials in the formulation. Due to the shrinkage or expansion of the resin and solvent, the combined volume occupied by the resin and solvent can be the same, greater or less than the combined volume of the individual components. The second factor affecting the volume of the dry paint formulation is the extent to which the space between the pigment particles is filled by the adhesive.

Above and close to the critical pigment volume concentration, the volume of dry paint film is larger than the theoretical volume, which is due to the increase of unfilled voids between pigment particles. The porosity of the film means that this approach is not appropriate.

The volume value of the non-volatile matter depends on the temperature and time of heating, and these conditions should be carefully considered for the material under test.

1 Champ d'application
This document specifies a method for determining the non-volatile material volume (NV V) of coatings and related products by measuring the density of dried coatings over any specified temperature range and drying or curing periods. This method is used to determine the non-volatiles immediately after use.

Using the volume results of the non-volatile matter obtained according to this document, the spread rate of the coating material can be calculated.

The method specified in this document is the selection method for air drying materials. Its use of other materials has not been tested.

Annex B provides an overview of available methods for determining the content and volume of nonvolatile substances.

This document does not apply to coatings exceeding the critical pigment volume concentration.

OIN 3233-1-2019 “Peintures et vernis-détermination des composés non volatils en pourcentage volume – Partie 1: Procédé pour la détermination de composés non volatils à l'aide de plaques d'essai revêtues et pour la détermination de la densité du film sec selon le principe Akimid”

2 Documents normatifs de référence
Lorsque les documents suivants sont mentionnés dans le texte, une partie ou la totalité de leur contenu constitue les exigences de ce document. Pour les références datées, seule la version citée s'applique. Pour les citations non datées, la nouvelle version du document de citation (y compris toutes les révisions) s'applique.

OIN 1513, Peintures et vernis — Inspection et préparation des échantillons de test

OIN 2811 (toutes les parties), peintures et vernis — Détermination de la densité

OIN 4618, Peintures et vernis — Termes et définitions

OIN 15528, Des peintures, vernis et matières premières pour peintures et vernis — Échantillonnage

3 Termes et définitions
Aux fins de ce document, les termes et définitions donnés dans l'ISO 4618 and the following shall apply.

L'ISO et la CEI maintiennent des bases de données terminologiques pour la normalisation aux adresses suivantes:

– Plateforme de navigation en ligne ISO: iso.org/obp

— Électropédie CEI:electropedia.org/ obtained

3.1 Non-volatile substances

Mass residue obtained by evaporation under specified conditions

Note d'entrée 1: Instead of the term “matière non volatile”, different terms such as solid, dry residue, dry matter, solid matter, drying residue are usually used with their respective abbreviations. Le terme “non-volatile substance”, also used in ISO 3251, should be used together with the abbreviation “NV” instead of these terms.

Note 2: This document and ISO 3251 specify different conditions for the determination of NV. Donc, in this document, the symbol NV m is used for non-volatile substances by mass.

[Source: OIN 4618:2014 2.176 modifié — Note 2 added to entry.]

3.2 Non-volatile volume NVV

Volume percent residue obtained by evaporation under specified conditions

OIN 3233-1-2019 “Peintures et vernis-détermination des composés non volatils en pourcentage volume – Partie 1: Procédé pour la détermination de composés non volatils à l'aide de plaques d'essai revêtues et pour la détermination de la densité du film sec selon le principe Akimid”

3.3 Transmission rate s

Une certaine quantité de peinture peut recouvrir la surface pour fournir l'épaisseur souhaitée du film sec

Note 1: Exprimé en m 2 /l ou m 2 /kg.

[Source: OIN 4618:2014, 2.238 — modified to add symbol and remove note 2 of entry.]

3.4 Practical dry film density ρ

Actually determine the density of dry and cured coatings

Seul le composant d'information standard est accessible au public. Pour voir le contenu complet, vous devrez acheter les normes via des canaux formels.