Signification et utilisation
4.1 Les films de peinture intérieure se salissent souvent, surtout près des portes, Fenêtres et aires de jeux, and often need to be cleaned by scrubbing. This test method covers the determination of the relative resistance of paint to erosion during scrubbing.

4.2 At absolute physical values (par exemple. cycle to failure for test method D2486 or microrise per 100 cycles for this test method), the accuracy of the scrub resistance measurement is poor due to the relatively large influence of subtle and difficult to control variables under the test conditions. The test method described herein minimizes this problem by using a standard calibration panel as an integral part of each scrubbing operation and correlating its weight loss to the weight loss of the film under test to determine the scrubbing resistance of the latter.

Note 1: The value of scrub resistance obtained through this test method is only relevant to the specific calibration panel type for which the value was obtained. Ainsi, Par exemple, a scrub resistance value of 83 for an X-type calibration panel would be reported as 83X.

4.3 The results obtained by this test method are not necessarily representative of the scrubbing resistance that may be determined if the test film is allowed to dry before the test is significantly longer than the seven-day period specified here.

4.4 The results obtained by this test method are not necessarily related to the ease of dirt or stain removal (aussi connu sous le nom “cleanability” ou “cleanability”). To test these characteristics, use test methods D3450 and D4828.

STM D4213-2016 “Méthode d'essai standard pour déterminer la résistance au frottement des revêtements par perte de poids d'usure”

Rayon
1.1 This test method covers an accelerated procedure for determining the resistance of paint to erosion caused by scrubbing. (Note: The term wet wear is sometimes used for scrubbing, and wet wear or scrubbability is used for scrubbing resistance. While scrubbing resistance tests are primarily used for internal coatings, they are sometimes used in conjunction with external coatings as an additional measure of film performance.

1.2 Les valeurs exprimées en unités SI doivent être considérées comme standard. Les valeurs données entre parenthèses sont à titre indicatif uniquement.

1.3 Cette norme n'est pas destinée à répondre à tous les problèmes de sécurité, si seulement, associé à son utilisation. Il est de la responsabilité des utilisateurs de cette norme d'établir des pratiques de sécurité et de santé appropriées et de déterminer l'applicabilité des restrictions réglementaires avant utilisation..