משמעות ותכלית

4.1 פגיעה בציפויי צינורות היא כמעט בלתי נמנעת במהלך הובלה ובנייה. A break or breach in the pipe coating may expose the pipe to corrosion because after the pipe is installed underground, the surrounding soil will contain moisture and constitute effective electrolytes. פוטנציאל ההגנה הקתודי המופעל עלול לגרום להתרופפות הציפוי, החל מקצה החג. Spontaneous holidays may also be caused by such potentials. This test method provides an accelerated condition for the occurrence of cathodic stripping and provides a measurement of the resistance of the coating to such actions.

4.2 The test effect shall be evaluated by physical inspection and monitoring the current consumed by the specimen. Usually there is no correlation between these two evaluation methods, but both methods are significant. The physical examination consists of assessing the effective contact of the coating with the metal surface based on the observed relative adhesion differences. It is often found that the cathodic stripping region extends from the region where adhesion is zero to the region where adhesion reaches the original level. There may also be intermediate regions of reduced adhesion.

4.3 ההנחות הקשורות לתוצאות הבדיקה כוללות:

4.3.1 Maximum adhesion or bonding is found in the coating not immersed in the test liquid, ו

4.3.2 The decreased adhesion in the immersion test area is the result of cathode stripping.

ASTM G42-11-2019 שיטת בדיקה סטנדרטית להפשטה קתודית של ציפוי צנרת בטמפרטורות גבוהות

4.4 Peel resistance is a desirable quality on a comparative basis, but peel in this test method is not necessarily an unfavourable indicator of coating performance. The advantage of this test method is that all the dielectric type coatings now commonly used peel off to some extent, ובכך מספקת דרך להשוות ציפוי אחד לאחר.

4.5 The current density in this test method is much higher than the current density usually required for cathodic protection in natural environment.

4.6 Any relatively small bonding area is caused by the combination of electrical stress with high and/or low temperatures and not due to anomalies in the application process. Relatively speaking, peel resistance is a professional quality, but most insulation materials will undergo some degree of peel under the accelerated conditions of this test. Bond strength is more important for proper functioning of some coatings than others, and the same measured peeling of two different coating systems may not represent an equivalent loss of corrosion protection.

4.6.1 The current flow through the test battery may be a relative indicator of the area to be protected against corrosion; למרות זאת, צפיפות הזרם הקיימת בבדיקה זו גדולה בהרבה מאלה הנדרשות בדרך כלל להגנה על קתודות בסביבות קרקע טבעיות בפנים הארץ.

ASTM G42-11-2019 שיטת בדיקה סטנדרטית להפשטה קתודית של ציפוי צנרת בטמפרטורות גבוהות

4.6.2 Test voltages higher than the recommended values may result in chlorine formation. Subsequent chemical effects on the coating may cast doubt on the interpretation of the test results.

היקף של

1.1 This test method describes an accelerated procedure for determining the comparative characteristics of an insulating coating system applied to the exterior of a steel pipe with the aim of preventing or mitigating corrosion that may occur in underground service where the pipe is exposed to high temperatures and under cathode-protection. The test method is intended for use on coated pipe samples obtained from commercial production and is applicable to samples where the coating has an electrical barrier function.

1.2 This test method is used to test coatings immersed or submerged in test solution at high temperature. When it is impractical to submerge or immerse the specimen, the use of test method G95, in which the test unit is bonded to the surface of the coated pipe specimen, may be considered. If room temperature is required, see Test Method G8. If you need a specific test method without options, see Test Method G80.

1.3 The value of three valid decimals retained in SI units shall prevail. הערכים המופיעים בסוגריים הם לעיון בלבד.

1.4 Warnings – Mercury has been designated by the EPA and many state agencies as a hazardous substance that can cause damage to the central nervous system, kidney, and liver. Mercury or its vapors may be hazardous to health and corrodes materials. Care should be taken when handling mercury and products containing mercury. For more information, please refer to the applicable Product Material Safety Data Sheets (MSDS) and for additional information, please refer to the EPA website (epa.gov/mercury/faq.htm). Users should be aware that in your state, state laws may prohibit the sale of mercury or mercury-containing products, or both.

ASTM G42-11-2019 שיטת בדיקה סטנדרטית להפשטה קתודית של ציפוי צנרת בטמפרטורות גבוהות

1.5 תקן זה לא נועד לטפל בכל נושאי הבטיחות, אם בכלל, הקשורים לשימוש בו. באחריות המשתמשים בתקן זה לבסס בטיחות מתאימה, שיטות בריאות וסביבתיות ולקבוע את תחולתן של הגבלות רגולטוריות לפני השימוש.

1.6 תקן בינלאומי זה פותח בהתאם לעקרונות התקינה המקובלים בעולם שנקבעו בהחלטות של החסמים הטכניים למסחר (TBT) הוועדה של ארגון הסחר העולמי לגיבוש תקנים בינלאומיים, הנחיות ועקרונות מומלצים.