Significato e scopo
5.1 In alcuni casi, coating damage applied to the substrate under typical conditions of use is unacceptable. It has been found that the test method can be used to distinguish the damage degree of coating on the substrate. It is useful to provide relative ratings for a range of coated plates that exhibit significant differences in damage.

5.2 In limited laboratory studies, it is not possible to obtain meaningful damage results when testing powder coatings. Scratches, or scratches, become increasingly imperceptible over time. Perciò, powder coatings may not be suitable for this test method.

Ambito di applicazione
1.1 This test method covers the determination of abrasion resistance on smooth, flat surfaces. The results are expressed in terms of tear force films when organic coatings, come la vernice, vernice, and lacquer, are applied to smooth, flat panel surfaces.

ASTM D5178-2021 Abrasion Resistance of Organic Coatings

1.2 Units-Values expressed in inch-pound units are considered standard. I valori indicati tra parentesi sono trasformazioni matematiche delle unità SI e sono solo di riferimento e non sono considerati standard.

1.3 Questo standard non è destinato ad affrontare tutti i problemi di sicurezza, se presente, legati al suo utilizzo. È responsabilità degli utenti di questo standard stabilire una sicurezza adeguata, pratiche sanitarie e ambientali e per determinare l'applicabilità delle restrizioni normative prima dell'uso.

1.4 La presente norma internazionale è stata sviluppata in conformità con i principi di standardizzazione accettati a livello internazionale stabiliti nelle decisioni del Comitato sugli ostacoli tecnici agli scambi (TBT) dell’Organizzazione Mondiale del Commercio sulla formulazione di norme internazionali, linee guida e principi raccomandati.