意味と目的
4.1 The test method measures the degree to which the sharp corners are covered by different coating powder materials. Corner coverage is affected by surface thickness, thixotropy, melt viscosity, 表面張力, curing rate, and application and curing temperature.

の範囲
1.1 The test method consists of determining the ratio of angular thickness (見る 3.1.3) to face thickness (見る 3.1.4) of a powder coating applied to a specific face thickness by immersing a preheated square rod in an aerated powder and curing the coating with predetermined conditions.

ASTM D 2967-2017 “粉体塗装のコーナー塗装”

注記 1: The property of corner coverage is also known as “edge coverage”, but the latter is not recommended. There are widespread misconceptions and expectations about the term “edge coverage”. The test was performed on rebar with square angles and the results are not necessarily associated with sharper edges, namely burrs. Coatings with measurable corner coverage may still not protect sharper edges from corrosion or provide the electrical insulation required for some applications.

1.2 SI単位で表した値を基準とします。. 括弧内の値は参考値です。.

1.3 この規格は、すべての安全問題に対処することを目的としたものではありません, もしあれば, その使用に関連する. 適切な安全衛生慣行を確立し、使用前に規制上の制限の適用可能性を判断することは、この規格のユーザーの責任です。.

1.4 この国際規格は、国際規格開発の原則に関する決定で確立された国際的に認められた標準化原則に従って開発されました。, 世界貿易機関の貿易の技術的障壁に関する委員会が発行したガイドラインと勧告.