意味と目的
3.1 この試験方法は特にフリーフィルムの測定に適しています。, and also suitable for the measurement of films on laboratory test plates.

3.2 The accuracy and accuracy of the thickness measurement may be affected by the deformation ability of the coating. This test method is not applicable to coatings that are prone to deformation under the load of the measuring instrument.

3.3 When the coating is applied to laboratory test plates, the accuracy and accuracy of the thickness measurement is also affected by the uniformity of the substrate.

の範囲
1.1 This test method includes the use of a micrometer to measure the dry film thickness of paint, varnisher, lacquer and related products. Programs A and B used fixed micrometers, and programs C and D used handheld micrometers. Procedures A and C are not recommended for films less than 12.5 μm (0.5 mille) in thickness. The minimum thickness required for procedures B and D is a function of the minimum thickness required to be able to remove the sample as a free film.

1.2 The following procedures appear:

1.2.1 Procedure A — Fixed micrometer for measuring flat rigid surface coatings.

1.2.2 Procedure B — Fixed micrometer for measuring free film.

1.2.3 Program C — Handheld micrometer for measuring coatings on flat rigid surfaces.

1.2.4 Program D — Handheld micrometer for measuring free films.

1.3 SI 単位で表される値が優先されます。. 括弧内の値は参考値です。.

ASTM D1005-95-2020 マイクロメーターを使用して有機コーティングの乾燥膜厚を測定するための標準試験方法

1.4 この規格は、すべての安全問題に対処することを目的としたものではありません, もしあれば, その使用に関連する. 適切な安全性を確立するのは、この規格のユーザーの責任です。, 健康および環境慣行を確認し、使用前に規制制限の適用可能性を判断するため.

1.5 この国際規格は、国際規格開発の原則に関する決定で確立された国際的に受け入れられた標準化原則に従って開発されました。, 貿易の技術的障壁によって発行されたガイドラインと推奨事項 (未定) 世界貿易機関委員会.