意味と使い方

3.1 水スプレーによる洗浄 (SSPC-TR2 / ネイス6G 198; SSPC-SP 5 (WAB)/バースワブ-1; SSPC-SP 10 (WAB)/ボーン WAB-2; SSPC-SP 6 (WAB)/NACE WAB-3; SSPC-SP 14 (WAB)/NACE WAB-8); SSPC-SP 7 (WAB)/NACE WAB-4 or not, (SSPC-SP WJ-1 / NACE WJ-1; SSPC-SP WJ-2 / NACE WJ-2; SSPC-SP WJ-3 / NACE WJ- 3; SSPC-SP WJ-4 / NACE WJ-4) 研磨剤, which can cause flash rust under certain environmental conditions. Inhibitors are used to prevent flash rust during drying and before coating. The inhibitor or the reaction product of the inhibitor on the substrate becomes part of the coating system. Coating properties may be affected by inhibitors. Soluble contaminants or unreacted inhibitors beneath the coating may cause premature failure.

3.2 The user or illustrator needs to determine the specific test method and exposure conditions to be used. Some of the referenced test methods may not be applicable to all types of coatings.

ASTM D5367-16 “表面に適用されるコーティングの評価の標準的な方法では、水または水/研磨サンドブラストによる鋼のフラッシュ錆を防ぐために、抑制剤で処理されます。.

範囲

1.1 この実践には、コーティング前に鋼鉄の錆を防ぐために使用されるコーティングとコーティングの適合性を評価する手順が含まれます。.

1.2 抑制剤は、研磨剤の有無にかかわらず、水スプレーによる洗浄表面処理と組み合わせて使用​​できます。.

1.3 防止剤と塗料の適合性を確認するには、塗料メーカーに相談する必要があります。.

1.4 この規格は、すべての安全問題に対処することを目的としたものではありません, もしあれば, その使用に関連する. この規格のユーザーは、使用前に適切な安全衛生慣行を確立し、規制上の制限の適用可能性を判断する責任があります。.