의미와 목적
5.1 도장된 금속의 실외 부식은 다음을 포함한 여러 요인의 영향을 받습니다.: 부식성 분위기, 비, 응축된 이슬, ultraviolet light, wet/dry cycle and temperature cycle. These factors often have synergistic effects on each other. This practice is intended to provide a more realistic simulation of the interaction of these factors than conventional testing with continuous exposure to a set of static corrosion conditions.

5.2 The results obtained from this exercise can be used to compare the relative durability of materials subjected to a particular test cycle.

5.3 No exposure test can be specified as a complete simulation of actual conditions of use in outdoor environments. Only when a rank correlation has been established for the particular material being tested can the results obtained from the exposure performed according to this practice be considered representative of the actual outdoor exposure. The relative durability of materials in actual outdoor service can vary considerably from location to location due to differences in UV radiation, 젖은 시간, 온도, 오염물질, 그리고 다른 요인. 따라서, even if results from specific artificial test conditions are found to be useful for comparing the relative durability of materials exposed to specific external environments, it cannot be assumed that they can be used to determine the relative durability in different environments.

5.4 Although very tempting, it is not recommended to calculate an “acceleration factor” that relates x hours of laboratory exposure to y months of external exposure. Different materials and different formulations of the same material may have significantly different acceleration coefficients. The acceleration factor also varies according to changes in degradation rates in laboratory tests and actual outdoor exposures.

5.5 This practice is suitable for comparing the relative performance of materials tested simultaneously in the same exposure device. Since there may be differences between the same type of exposure equipment, it is not recommended to compare the amount of degradation in different equipment exposed to the same duration of material at different times or running the same test conditions. This practice should not be used to establish “통과 실패” approvals for materials after a specific exposure period unless performance is compared relative to control materials exposed at the same time or variability in testing is rigorously quantified so that statistically significant pass/fail judgments can be made.

5.6 This practice has been found to be useful for air-dried industrial maintenance coatings on steel 3,4,5,6,7 and zinc-rich primers, but its applicability in high UV stability coating systems, such as automotive applications, has not been evaluated.

ASTM D 5894-2021 “순환 염수 분무/도장 금속의 UV 노출 (또는 염수 분무/건조 챔버 및 UV/응축기 챔버에 노출)”

범위
1.1 The practice covers the fundamentals and operational practices of cyclic corrosion/UV exposure of paint on metal, with alternate exposure in two different cabinets: a cyclic salt spray/drying cabinet and a fluorescent UV/condensing cabinet.

1.2 This practice is limited to methods and procedures for obtaining, measuring and controlling exposure conditions. It does not specify the preparation of the specimens or the evaluation of the results.

1.3 SI 단위로 표현된 값은 표준값으로 간주되어야 합니다.. 다른 측정 단위는 이 표준에 포함되지 않습니다..

1.4 이 표준은 모든 안전 문제를 다루기 위한 것이 아닙니다., 만약에 어떠한, 그 사용과 관련된. 적절한 안전을 확립하는 것은 이 표준 사용자의 책임입니다., 건강 및 환경 관행을 확인하고 사용 전 규제 제한의 적용 여부를 결정합니다..

1.5 본 국제 표준은 국제 표준 개발 원칙에 관한 결정에서 확립된 국제적으로 인정받는 표준화 원칙에 따라 개발되었습니다., 세계무역기구(WTO) 무역기술장벽위원회가 발행한 지침 및 권고사항.