ASTM B530 Standaard testmethode voor magnetische meting van laagdikte: Electrodeposited Nickel Coatings on Magnetic and non-magnetic Substrates includes non-destructive measurement of the thickness of electrodeposited nickel coatings on magnetic or non-magnetic substrates using a magnetic instrument.
Betekenis en gebruik

5.1 De dikte van de coating is over het algemeen belangrijk voor de prestaties ervan. This magnetic method is suitable for non-destructive measurement of thickness and specification acceptance of certain nickel coatings.

5.2 The method requires that the magnetic properties of the coating and its substrate be the same as those of the reference standard used for instrument calibration adjustment.

5.3 The method should not be used to determine the thickness of self-catalyzed deposited nickel-phosphorus alloys containing more than 8% P in steel. As long as the measurements are made prior to any heat treatment, those coatings are sufficiently non-magnetic for test method B499 to be suitable for the determination.

B530-2014 “Standaard testmethode voor het meten van de laagdikte met behulp van een magnetische methode: Elektrolytisch afgezette nikkelcoatings op magnetische en niet-magnetische substraten”

Stap 1: Domein

1.1 This test method includes non-destructive measurement of the thickness of an electrodeposited nickel coating on a magnetic or non-magnetic substrate using a magnetic instrument. Het is bedoeld als aanvulling op de instructies van de fabrikant over de bediening van het instrument, niet om ze te vervangen.

1.2 These instruments measure the magnetic attraction between the magnet and the coating – substrate combination (geclassificeerd als “magnetic pull-off”), or the change in magnetic flux density within the probe (geclassificeerd als “elektron”).

1.3 For this test method, two types of coating-substrate combinations can be encountered: Type A, nickel coatings on magnetic substrates, and Type B nickel coatings on non-magnetic substrates.

1.4 The effective measurement range of instruments using the magnetic attraction principle is up to 50μm (2 Mil) for type A coatings and up to 25μm (1 mil) for type B coatings. For gauges based on the principle of flux density variation, the effective range is much larger and measurements up to 1 mm (40 Mil) or higher can be made on both types of coatings.

1.5 Measurements made in accordance with this test method shall comply with the requirements of ISO Standard 2361, afgedrukt 1982.

1.6 Waarden uitgedrukt in SI-eenheden worden als standaard beschouwd. De waarden tussen haakjes zijn alleen ter referentie.

1.7 Deze norm is niet bedoeld om alle veiligheidsproblemen aan te pakken, indien aanwezig, die verband houden met het gebruik ervan. Het is de verantwoordelijkheid van gebruikers van deze norm om passende veiligheids- en gezondheidspraktijken vast te stellen en voorafgaand aan gebruik de toepasbaarheid van wettelijke beperkingen te bepalen..