Significado e Propósito
4.1 The test method measures the degree to which the sharp corners are covered by different coating powder materials. Corner coverage is affected by surface thickness, thixotropy, melt viscosity, tensão superficial, curing rate, and application and curing temperature.

Escopo de
1.1 The test method consists of determining the ratio of angular thickness (ver 3.1.3) to face thickness (ver 3.1.4) of a powder coating applied to a specific face thickness by immersing a preheated square rod in an aerated powder and curing the coating with predetermined conditions.

ASTM-D 2967-2017 “Revestimento de canto de revestimentos em pó”

Observação 1: The property of corner coverage is also known as “edge coverage”, but the latter is not recommended. There are widespread misconceptions and expectations about the term “edge coverage”. The test was performed on rebar with square angles and the results are not necessarily associated with sharper edges, namely burrs. Coatings with measurable corner coverage may still not protect sharper edges from corrosion or provide the electrical insulation required for some applications.

1.2 Os valores expressos em unidades do SI serão considerados padrões. Os valores dados entre parênteses são apenas para referência.

1.3 Esta norma não se destina a abordar todas as questões de segurança, caso existam, associado ao seu uso. É responsabilidade dos usuários desta norma estabelecer práticas adequadas de segurança e saúde e determinar a aplicabilidade das restrições regulatórias antes do uso..

1.4 Esta Norma internacional foi desenvolvida de acordo com os princípios de padronização internacionalmente reconhecidos estabelecidos na Decisão sobre Princípios para o Desenvolvimento de Normas Internacionais, Diretrizes e recomendações emitidas pelo Comitê sobre Barreiras Técnicas ao Comércio da Organização Mundial do Comércio.