Significado e Propósito
4.1 Danos aos revestimentos de tubos são quase inevitáveis ​​durante o transporte e a construção. Breaking or peeling of the pipe coating may expose the pipe to possible corrosion because after the pipe is installed underground, the surrounding soil will be moist and will constitute effective electrolytes. O potencial de proteção catódica aplicado pode fazer com que o revestimento se solte, começando no feriado. Spontaneous holidays may also be caused by this potential. Tipicamente, external pipe coatings coated on pipes carrying thermal media (óleo, gás) are exposed to high temperatures inside the pipe and low temperatures outside, and are subject to temperature gradients. The heat flux is directed from the metal (substrato) to the coating. The test method provides accelerated conditions for cathodic stripping that occurs under simulated heating and provides a measurement of the resistance of the coating to such effects.

4.2 The effect of the test will be evaluated by physical examination and monitoring the current consumed by the test sample. Usually there is no correlation between the two evaluation methods, but both are significant. The physical examination involves assessing the effective contact of the coating with the metal surface based on the observed difference in relative adhesive bonding. It is often found that the cathodic debonding region propagates from the region where adhesion is zero to the region where adhesion has reached the original level. There may also be intermediate areas of reduced adhesion.

4.3 As suposições relacionadas aos resultados do teste incluem:

ASTM-D 6676-2021 “Determinação da esfoliabilidade catódica de revestimentos de paredes de tubos após aquecimento pelo método de aquecimento interno”

4.3.1 The maximum adhesion or bonding force is found in the coating not immersed in the test liquid, e

4.3.2 The reduced adhesion in the immersion test area is the result of cathode debonding.

4.4 On a comparative basis, the ability to resist stripping is of professional quality, but stripping in this test method is not necessarily an unfavourable indication of coating performance. The advantage of this test method is that all the dielectric type coatings that are now commonly used destick to some extent, proporcionando assim uma maneira de comparar um revestimento com outro.

4.5 The current flow in the test unit is a relative indicator of the extent of the area requiring corrosion protection; No entanto, as densidades de corrente presentes neste teste são muito maiores do que aquelas normalmente exigidas para proteção de cátodos em ambientes naturais de solo interior.

4.6 Test voltages higher than the recommended voltage may cause chlorine gas formation. Subsequent chemical effects on the coating may call into question the interpretation of the test results. A filter tube with a sintered disk (see test method G95) or a sand layer (40 mesh) on the coated surface can reduce this effect.

ASTM-D 6676-2021 “Determinação da esfoliabilidade catódica de revestimentos de paredes de tubos após aquecimento pelo método de aquecimento interno”

Escopo de
1.1 This test method describes an accelerated procedure for determining the comparative characteristics of a coating system applied to the exterior of a steel pipe to prevent or mitigate corrosion that may occur underground or in water where the pipe carries a heating medium and is under cathodic protection. The test method is intended for use on samples of coated tubes, or specimens cut from coated tubes or plate parts, and is applicable to such samples when the coating has an electrical barrier function.

1.2 The test method is designed to simulate the exposure of the outer coating to the high temperature inside the pipe and the ambient temperature outside, thus being affected by the temperature gradient. If high temperature is required but no temperature gradient is available, see Test Method G42.

1.3 Valores expressos em unidades SI ou unidades polegada-libra devem ser tratados separadamente como valores padrão. Os valores especificados em cada sistema não são necessariamente os mesmos; Portanto, para garantir o cumprimento das normas, cada sistema deve ser usado independentemente um do outro e os valores dos dois sistemas não devem ser combinados.

ASTM-D 6676-2021 “Determinação da esfoliabilidade catódica de revestimentos de paredes de tubos após aquecimento pelo método de aquecimento interno”

1.4 Esta norma não se destina a abordar todas as questões de segurança, caso existam, associado ao seu uso. É responsabilidade do usuário desta norma estabelecer medidas de segurança apropriadas, práticas de saúde e ambientais e para determinar a aplicabilidade de restrições regulatórias antes do uso.

1.5 Esta Norma internacional foi desenvolvida de acordo com os princípios de padronização internacionalmente reconhecidos estabelecidos na Decisão sobre Princípios para o Desenvolvimento de Normas Internacionais, Diretrizes e recomendações emitidas pelo Comitê sobre Barreiras Técnicas ao Comércio da Organização Mundial do Comércio.