ASTM B530 Стандартный метод испытаний для магнитного измерения толщины покрытия: Electrodeposited Nickel Coatings on Magnetic and non-magnetic Substrates includes non-destructive measurement of the thickness of electrodeposited nickel coatings on magnetic or non-magnetic substrates using a magnetic instrument.
Значение и использование

5.1 Толщина покрытия, как правило, важна для его эксплуатационных характеристик.. This magnetic method is suitable for non-destructive measurement of thickness and specification acceptance of certain nickel coatings.

5.2 The method requires that the magnetic properties of the coating and its substrate be the same as those of the reference standard used for instrument calibration adjustment.

5.3 The method should not be used to determine the thickness of self-catalyzed deposited nickel-phosphorus alloys containing more than 8% P in steel. As long as the measurements are made prior to any heat treatment, those coatings are sufficiently non-magnetic for test method B499 to be suitable for the determination.

Б530-2014 “Стандартный метод испытаний для измерения толщины покрытия магнитным методом: Электроосажденные никелевые покрытия на магнитных и немагнитных подложках”

Шаг 1: Объем

1.1 This test method includes non-destructive measurement of the thickness of an electrodeposited nickel coating on a magnetic or non-magnetic substrate using a magnetic instrument. Он предназначен для дополнения инструкций производителя по эксплуатации прибора., не заменять их.

1.2 These instruments measure the magnetic attraction between the magnet and the coating – substrate combination (классифицируется как “magnetic pull-off”), or the change in magnetic flux density within the probe (классифицируется как “электрон”).

1.3 For this test method, two types of coating-substrate combinations can be encountered: Введите, nickel coatings on magnetic substrates, and Type B nickel coatings on non-magnetic substrates.

1.4 The effective measurement range of instruments using the magnetic attraction principle is up to 50μm (2 мил) for type A coatings and up to 25μm (1 мил) for type B coatings. For gauges based on the principle of flux density variation, the effective range is much larger and measurements up to 1 мм (40 мил) or higher can be made on both types of coatings.

1.5 Measurements made in accordance with this test method shall comply with the requirements of ISO Standard 2361, напечатано в 1982.

1.6 Значения, выраженные в единицах СИ, считаются стандартными.. Значения, указанные в скобках, предназначены только для справки..

1.7 Настоящий стандарт не предназначен для решения всех проблем безопасности., если таковые имеются, связанный с его использованием. Пользователи настоящего стандарта обязаны установить соответствующие правила техники безопасности и охраны труда, а также определить применимость нормативных ограничений перед использованием..