Aluminum silicate fiber is widely used in construction in recent years, shipbuilding, aviation and other fields of a new type of material, its main raw materials are high quality aluminum silicate material. Specifically, the main composition of aluminum silicate fiber including silicate and alumina, function and benefits of these ingredients for molybdenum silicate fiber has a great influence. First of all, silicate aluminum silicate fiber composition contains rich silicon, these elements in the material with stability and high temperature resistance, can prolong the service life of aluminum silicate fiber, and not easy to produce the problem such as thermal expansion and thermal crack, which can keep high strength under the environment of high temperature and high stability. Second, silicate also can improve the corrosion resistance of aluminum silicate fiber, make its can resist chemical corrosion and acid and alkali erosion. For the aluminum silicate fiber application in the field of Marine chemical industry and so on is very important

In addition to the silicate and alumina is one of the major components of aluminum silicate fiber. Alumina can enhance high temperature strength and the tensile properties of aluminum silicate fiber, make its can bear high temperature, high pressure and high load such as environmental challenges. In addition, the alumina also has good insulationPerformance, can effectively isolate current and prevent electrostatic accumulation, guarantee the safety of the production and use.

Spectrometer EDX9000B Plus tabletting method for rapid analysis aluminum silicate fiber raw material composition

As a kind of common high temperature insulation materials, aluminum silicate fiber in iron and steel, electric power, petrochemical and other industries has been widely used. Molybdenum silicate fiber raw material composition has a great influence on its performance and quality, so the raw material of molybdenum silicate fiber ingredients for rapid analysis, detection and control become a necessary step in the process of its production. Spectrometer EDX9000B Plus tabletting method as a raw material for efficient and accurate analysis method, has many advantages and advantages

EDX9000B plus spectrometer has the miniaturization, high performance, high speed, easy to operate, Na11 – U92 high sensitivity, high accuracy analysis; At the same time analysis of 40 kinds of elements; Using multiple collimator filter and buckle background patented technology; Peltier electric refrigeration FAST SDD silicon drift detector provides excellent short-term repeatability and reproducibility for a long time and good elements of the peak resolution; Ultra-high count multichannel digital circuit design, the double vacuum pumping speed, automatic vacuum stability system; Standard method of software, basic parameters of multitasking, multi-window operation; Patent membrane filter technology, effectively improve the light detection limit, etc.

Spectrometer EDX9000B Plus tabletting method for rapid analysis aluminum silicate fiber raw material composition

The use of spectrometer EDX9000B Plus tablet method to quickly analyze the raw material composition of aluminum silicate fiber operation steps are as follows:

1. Prepare the sample: the aluminum silicate fiber raw materials are broken and mixed, and about 2g samples are taken.

2. Preparation of sample pressing: Place 2g sample in the pressing mold, add about 0.3g of pressing tablet (KBr), and compress it into sheets.

3. Perform sample analysis:

Connect the spectrometer EDX9000B Plus power supply and open the software to connect the spectrometer to the computer;

The prepared aluminum silicate fiber laminate sample is fixed on the sampling table, select the corresponding analysis mode;

The composition and content of the sample were obtained through the interpretation of the spectrogram.

Using spectrometer EDX9000B Plus tabletting method for rapid analysis of aluminum silicate fiber raw material composition to precise and quick determination of the main element and its content in the aluminum silicate fiber raw materials, such as Si02, A1203, Fe203 etc. Also can to nondestructive analysis of samples, thus can reduce or eliminate destructive samples, and keep the integrity of the sample. And high accuracy, the advantages of good accuracy, repeatability, stability, can meet the requirements in the process of industrial production. Can effectively to control aluminum silicate fiber raw material composition, stability and consistency of the product.Using spectrometer EDX9000B Plus tabletting method test advantage obviously, also the specific advantages as follows:

Spectrometer EDX9000B Plus tabletting method for rapid analysis aluminum silicate fiber raw material composition

1. Without pretreatment, easy, save a lot of time and energy.

2. Samples for different type, shape, composition complexity and scope of content, has a good applicability.

3 is fast, efficient, accurate, reliable and precise analysis of the characteristics, to meet the high temperature insulation material production process of continuous, online and real time detection requirements.

4. With high resolution and detection limit, can achieve high analysis precision and accuracy.

5, tabletting method not only can be used for analysis of solid samples, can also be applied to the analysis of the liquid and gas samples, with a larger application range and flexibility.

Anyhow, spectrometer EDX9000B Plus tabletting method as raw materials for the aluminum silicate fiber analysis is an effective method, with simple operation, rapid, accurate and nondestructive precision analysis to the characteristics of the can for high temperature insulation materials industry production to provide strong support and guarantee for it.

The following is a spectrometer EDX9000B Plus tabletting method for rapid analysis of aluminum silicate fiber raw material composition test report: