ความหมายและวัตถุประสงค์
4.1 The test method measures the degree to which the sharp corners are covered by different coating powder materials. Corner coverage is affected by surface thickness, thixotropy, melt viscosity, surface tension, curing rate, and application and curing temperature.

ขอบเขตของ
1.1 The test method consists of determining the ratio of angular thickness (ดู 3.1.3) to face thickness (ดู 3.1.4) of a powder coating applied to a specific face thickness by immersing a preheated square rod in an aerated powder and curing the coating with predetermined conditions.

ASTM D 2967-2017 “การเคลือบมุมของการเคลือบผง”

บันทึก 1: The property of corner coverage is also known as “edge coverage”, but the latter is not recommended. There are widespread misconceptions and expectations about the term “edge coverage”. The test was performed on rebar with square angles and the results are not necessarily associated with sharper edges, namely burrs. Coatings with measurable corner coverage may still not protect sharper edges from corrosion or provide the electrical insulation required for some applications.

1.2 ค่าที่แสดงเป็นหน่วย SI ให้ถือเป็นมาตรฐาน. ค่าที่ระบุในวงเล็บมีไว้เพื่อการอ้างอิงเท่านั้น.

1.3 มาตรฐานนี้ไม่ได้มีวัตถุประสงค์เพื่อแก้ไขปัญหาด้านความปลอดภัยทั้งหมด, ถ้ามี, ที่เกี่ยวข้องกับการใช้งาน. เป็นความรับผิดชอบของผู้ใช้มาตรฐานนี้ในการกำหนดแนวทางปฏิบัติด้านความปลอดภัยและสุขภาพที่เหมาะสม และเพื่อพิจารณาการบังคับใช้ข้อจำกัดด้านกฎระเบียบก่อนใช้งาน.

1.4 มาตรฐานสากลนี้ได้รับการพัฒนาตามหลักการมาตรฐานที่ได้รับการยอมรับในระดับสากลซึ่งกำหนดไว้ในการตัดสินใจเกี่ยวกับหลักการเพื่อการพัฒนามาตรฐานสากล, แนวทางและข้อเสนอแนะที่ออกโดยคณะกรรมการว่าด้วยอุปสรรคทางเทคนิคต่อการค้าขององค์การการค้าโลก.