5.1 The coating attached to the substrate will be subject to destructive impact during the manufacturing and use of the product. It has been found that this impact-resistant practice helps predict the performance of organic coatings due to their ability to resist impact-induced cracking.

Сфера застосування
1.1 The practice covers procedures for determining the ability of the coating and its substrate to resist breakage, cracking or chipping when the film and substrate expand to their original form as a result of impact.

1.2 This practice does not measure impact resistance, but uses rapid impact to improve the test method D522, which is a flexible test method. Since the effect of the coating is almost instantaneous, all problems related to the time variable in the mand-axis test are eliminated.

ASTM D 6905-2020 Ударна в'язкість органічних покриттів

1.3 This practice is similar in content but not technically equivalent to test method D2794.

1.4 Values expressed in SI units should be considered standard. Значення, наведені в дужках, наведено лише для довідки.

1.5 Цей стандарт не призначений для вирішення всіх питань безпеки, якщо хто-небудь, пов'язані з його використанням. Відповідальність за встановлення належної безпеки несе користувач цього стандарту, здоров’я та навколишнього середовища, а також для визначення застосовності нормативних обмежень перед використанням.

1.6 Цей міжнародний стандарт розроблено відповідно до міжнародно визнаних принципів стандартизації, встановлених у Рішенні про принципи розробки міжнародних стандартів., Настанови та рекомендації, видані Комітетом з технічних бар’єрів у торгівлі Світової організації торгівлі.