ASTM B530 طريقة الاختبار القياسية للقياس المغناطيسي لسمك الطلاء: Electrodeposited Nickel Coatings on Magnetic and non-magnetic Substrates includes non-destructive measurement of the thickness of electrodeposited nickel coatings on magnetic or non-magnetic substrates using a magnetic instrument.
المعنى والاستخدام

5.1 سمك الطلاء مهم بشكل عام لأدائه. This magnetic method is suitable for non-destructive measurement of thickness and specification acceptance of certain nickel coatings.

5.2 The method requires that the magnetic properties of the coating and its substrate be the same as those of the reference standard used for instrument calibration adjustment.

5.3 The method should not be used to determine the thickness of self-catalyzed deposited nickel-phosphorus alloys containing more than 8% P in steel. As long as the measurements are made prior to any heat treatment, those coatings are sufficiently non-magnetic for test method B499 to be suitable for the determination.

B530-2014 “طريقة الاختبار القياسية لقياس سمك الطلاء بالطريقة المغناطيسية: طلاءات النيكل المرسبة كهربائياً على ركائز مغناطيسية وغير مغناطيسية”

خطوة 1: نِطَاق

1.1 This test method includes non-destructive measurement of the thickness of an electrodeposited nickel coating on a magnetic or non-magnetic substrate using a magnetic instrument. الغرض منه هو استكمال تعليمات الشركة المصنعة بشأن تشغيل الأداة, لا ليحل محلهم.

1.2 These instruments measure the magnetic attraction between the magnet and the coating – substrate combination (تصنف على أنها “magnetic pull-off”), or the change in magnetic flux density within the probe (تصنف على أنها “إلكترون”).

1.3 For this test method, two types of coating-substrate combinations can be encountered: نوع أ, nickel coatings on magnetic substrates, and Type B nickel coatings on non-magnetic substrates.

1.4 The effective measurement range of instruments using the magnetic attraction principle is up to 50μm (2 مل) for type A coatings and up to 25μm (1 ميل) for type B coatings. For gauges based on the principle of flux density variation, the effective range is much larger and measurements up to 1 مم (40 مل) or higher can be made on both types of coatings.

1.5 Measurements made in accordance with this test method shall comply with the requirements of ISO Standard 2361, طبع في 1982.

1.6 تعتبر القيم المعبر عنها بوحدات النظام الدولي (SI) قياسية. القيم الواردة بين قوسين هي للإشارة فقط.

1.7 لا يهدف هذا المعيار إلى معالجة جميع المخاوف المتعلقة بالسلامة, لو اي, المرتبطة باستخدامه. تقع على عاتق مستخدمي هذا المعيار مسؤولية إنشاء ممارسات السلامة والصحة المناسبة وتحديد إمكانية تطبيق القيود التنظيمية قبل الاستخدام..