Význam a účel
4.1 The test method measures the degree to which the sharp corners are covered by different coating powder materials. Corner coverage is affected by surface thickness, thixotropy, melt viscosity, surface tension, curing rate, and application and curing temperature.

Pohled do
1.1 The test method consists of determining the ratio of angular thickness (vidět 3.1.3) to face thickness (vidět 3.1.4) of a powder coating applied to a specific face thickness by immersing a preheated square rod in an aerated powder and curing the coating with predetermined conditions.

ASTM D 2967-2017 “Corner Coating of Powder Coatings”

Poznámka 1: The property of corner coverage is also known as “edge coverage”, but the latter is not recommended. There are widespread misconceptions and expectations about the term “edge coverage”. The test was performed on rebar with square angles and the results are not necessarily associated with sharper edges, namely burrs. Coatings with measurable corner coverage may still not protect sharper edges from corrosion or provide the electrical insulation required for some applications.

1.2 Hodnoty vyjádřené v jednotkách SI se považují za normy. Hodnoty uvedené v závorkách jsou pouze orientační.

1.3 Tato norma není určena k řešení všech bezpečnostních problémů, jestli nějaký, spojené s jeho užíváním. Je odpovědností uživatelů této normy zavést vhodné bezpečnostní a zdravotní postupy a určit použitelnost regulačních omezení před jejím použitím..

1.4 Tato mezinárodní norma byla vyvinuta v souladu s mezinárodně uznávanými normalizačními zásadami stanovenými v Rozhodnutí o zásadách pro vývoj mezinárodních norem., Směrnice a doporučení vydané Výborem pro technické překážky obchodu Světové obchodní organizace.