Arti dan Tujuan
4.1 The test method measures the degree to which the sharp corners are covered by different coating powder materials. Corner coverage is affected by surface thickness, thixotropy, melt viscosity, tegangan permukaan, curing rate, and application and curing temperature.

Ruang lingkup
1.1 The test method consists of determining the ratio of angular thickness (melihat 3.1.3) to face thickness (melihat 3.1.4) of a powder coating applied to a specific face thickness by immersing a preheated square rod in an aerated powder and curing the coating with predetermined conditions.

ASTM D 2967-2017 “Lapisan Sudut Lapisan Serbuk”

Catatan 1: The property of corner coverage is also known as “edge coverage”, but the latter is not recommended. There are widespread misconceptions and expectations about the term “edge coverage”. The test was performed on rebar with square angles and the results are not necessarily associated with sharper edges, namely burrs. Coatings with measurable corner coverage may still not protect sharper edges from corrosion or provide the electrical insulation required for some applications.

1.2 Nilai yang dinyatakan dalam satuan SI harus dianggap sebagai standar. Nilai yang diberikan dalam tanda kurung hanya untuk referensi.

1.3 Standar ini tidak dimaksudkan untuk mengatasi semua masalah keselamatan, jika ada, terkait dengan penggunaannya. Pengguna standar ini bertanggung jawab untuk menetapkan praktik keselamatan dan kesehatan yang sesuai dan menentukan penerapan pembatasan peraturan sebelum digunakan..

1.4 Standar internasional ini telah dikembangkan sesuai dengan prinsip-prinsip standardisasi yang diakui secara internasional yang ditetapkan dalam Keputusan Prinsip-Prinsip Pengembangan Standar Internasional, Pedoman dan Rekomendasi yang dikeluarkan oleh Komite Hambatan Teknis Perdagangan Organisasi Perdagangan Dunia.