1 Jangkauan
This standard specifies test methods for electroplating of silver and silver alloys for engineering, decoration and protection purposes against contamination by residual salts.

Standar ini berlaku untuk bagian logam; Tidak berlaku untuk komponen komposit, seperti bagian dengan plastik dan logam berlapis.

2 Prinsip
The part was boiled in water with known conductivity for a specified time and the increase in conductivity resulting from precipitation of residual salts and other conductive impurities was measured.

3 Reagen
Air: Konduktivitasnya tidak lebih dari 100µs/m pada 20 °C ±1 °C.

ISO 4522-3:1988 “Metode pengujian lapisan logam perak dan paduan perak – Bagian 3: Penentuan sisa garam”

4 Instrumen
Semua instrumen kaca yang digunakan harus terbuat dari kaca borosilikat, harus memenuhi persyaratan kebersihan yang ditentukan dalam 5.2, and shall be stored separately for this test.

4.1 Labu alas bulat: The capacity is 250mL, dan dipasang tabung kondensor refluks air.

4.2 Gelas kimia: Size suitable for the part under test, ditandai dengan skala 100mL, equipped with appropriate devices to reduce excessive evaporation loss of water, seperti penutup air pendingin.

4.3 Pengukur konduktivitas

5 Metode tes
5.1 Sampel

Take one or more fully coated metal parts with a total surface area of about 30cm2 and test according to the size (melihat 5.3) as specified in 5.3.1 atau 5.3.2.

Pastikan untuk menghindari kontaminasi sampel yang tidak disengaja, and bring clean gloves to the corner of the parts during the inspection.

5.2 Pemeriksaan kebersihan instrumen

Sebelum pengujian, 100mL air (lihat Bab 3) was added to the test container (melihat 4.1 atau 4.2) dan kemudian direbus perlahan selama 10 menit pada kondisi pengujian yang ditentukan (melihat 5.3.1 Dan 5.3.2). Airnya didinginkan hingga 20 °C ±1 °C dan konduktivitasnya diukur dengan alat pengukur konduktivitas (melihat 4.3).

Jika pengukuran melebihi 100µS/m, it was determined again with another 100mL of water. If the measurement value again exceeded 100µS/m, it was changed to a new vessel and tested again.

Qualified glass instruments should be stored separately for this test.

5.3 Pengukuran

5.3.1 Samples with cross section width or diameter less than 15mm and length less than 40mm.

Setelah memeriksa kebersihan alat (melihat 5.2), tempatkan sampelnya (melihat 5.1) into a round-bottom flask and add 100mL of water (lihat Bab 3). The electrical conductivity of the water should be determined quickly before the measurement. Celupkan seluruh benda uji ke dalam air. The reflow condenser tube was installed on the flask and slowly boiled for 10min. Airnya didinginkan hingga 20 °C ±1 °C, and the conductivity was measured with a conductivity meter (melihat 4.3). Nilai tambah konduktivitas dihitung sebagai hasil pengukuran.

ISO 4522-3:1988 “Metode pengujian lapisan logam perak dan paduan perak – Bagian 3: Penentuan sisa garam”

5.3.2 Sampel dengan lebar atau diameter penampang lebih besar dari 15 mm dan panjang lebih besar dari 40 mm.

The test was performed as described in 5.3.1. Tempatkan sampel (melihat 5.1) ke dalam gelas kimia (melihat 4.2) with water to 100mL scale. To PREVENT loss OF WATER from excessive evaporation during the assay, a cooling water hood may be used and, jika diperlukan, air tambahan (lihat Bab 3) dapat ditambahkan untuk menggantikan air yang diuapkan.

ISO 4522-3:1988 “Metode pengujian lapisan logam perak dan paduan perak – Bagian 3: Penentuan sisa garam”

6 Laporan pengujian
The test report shall include at least the following:

A) Referensi ke Standar ini;

B) Name or number of test sample;

The total surface area of the test sample,cm2; D) nama atau model instrumen yang digunakan;

Anomalies observed during testing; F) instruksi apa pun yang berbeda dari metode ini;

G) Test results and representation methods;

H) Tanggal tes;

Saya) Name of operator and testing laboratory.