Significato e scopo
4.1 La misurazione dello spessore del film bagnato aiuta a prevedere lo spessore del film secco. Wet film thickness is usually specified in cases where dry film thickness cannot be measured nondestructively. Inoltre, the ability to determine the wet film thickness during the application can provide the opportunity to correct the application.

Ambito di applicazione
1.1 This test method includes the determination of wet film thickness of organic coatings such as paint, varnisher and lacquer. The two methods are described as follows:

1.1.1 In test method A, wet film thickness was measured using a wet film thickness gauge (in imperial or metric scale (Vedere 5.1)) up to 60 mils in the imperial scale series and 700 μm in the metric scale series (Sections 5 — 8).

1.1.2 In test Method B, the Pfund Gage was used to measure wet film thickness up to 14.2 mil (360 micrometri) (Sections 9-13).

Metodo di prova standard ASTM D1212-2020 per la misurazione dello spessore del film umido di rivestimenti organici

1.2 Values expressed in SI units are treated as standards. I valori indicati tra parentesi sono solo di riferimento.

1.3 Questo standard non è destinato ad affrontare tutti i problemi di sicurezza, se presente, legati al suo utilizzo. È responsabilità degli utenti di questo standard stabilire una sicurezza adeguata, pratiche sanitarie e ambientali e per determinare l'applicabilità delle restrizioni normative prima dell'uso.

1.4 La presente norma internazionale è stata sviluppata in conformità con i principi di standardizzazione accettati a livello internazionale stabiliti nelle decisioni del Comitato sugli ostacoli tecnici agli scambi (TBT) dell’Organizzazione Mondiale del Commercio sulla formulazione di norme internazionali, linee guida e principi raccomandati.