4.1 Coatings with satisfactory performance need to adhere to the substrate to which they are applied. It has been found that the test method can be used to distinguish the degree of adhesion of the coating to the substrate. It is most applicable to provide a relative rating for a range of coated plates that exhibit significant differences in adhesion.

4.2 Studies conducted in the laboratory using the ring pen specified in the previous edition have shown that meaningful adhesion data are not possible when a load of 10 naar 20 kg is required to break the surface of the solvent-based coating. When a load of this magnitude is required, the chrome-plated ring stylus vibrates and jumps on the coated surface. Similar meaningless data were obtained when testing required more than 10kg of powder paint to destroy the surface. Daarom, testing under these conditions is not applicable.

ASTM D2197-16-2022 Evaluation of Adhesion of Organic Coatings by Scratch Method

Reikwijdte van

1.1 This test method covers the determination of adhesion of organic coatings such as paint, varnish and lacquer on smooth, vlak (vlak) panel surfaces.

1.2 Waarden uitgedrukt in SI-eenheden worden als standaarden beschouwd. De waarden tussen haakjes zijn alleen ter referentie.

1.3 Deze norm is niet bedoeld om alle veiligheidsproblemen aan te pakken, indien aanwezig, die verband houden met het gebruik ervan. Het is de verantwoordelijkheid van de gebruikers van deze norm om de juiste veiligheid te garanderen, gezondheids- en milieupraktijken en om vóór gebruik de toepasbaarheid van wettelijke beperkingen vast te stellen.

1.4 Deze internationale norm is ontwikkeld in overeenstemming met de internationaal aanvaarde standaardisatieprincipes die zijn vastgelegd in de besluiten van het Comité voor technische handelsbelemmeringen (TBT) van de Wereldhandelsorganisatie over de formulering van internationale normen, richtlijnen en aanbevolen principes.