Znaczenie i cel
4.1 Uszkodzenia powłok rur są prawie nieuniknione podczas transportu i budowy. Breaking or peeling of the pipe coating may expose the pipe to possible corrosion because after the pipe is installed underground, the surrounding soil will be moist and will constitute effective electrolytes. Zastosowany potencjał ochrony katodowej może spowodować poluzowanie powłoki, zaczynając od końca wakacji. Spontaneous holidays may also be caused by this potential. Typowo, external pipe coatings coated on pipes carrying thermal media (olej, gas) are exposed to high temperatures inside the pipe and low temperatures outside, and are subject to temperature gradients. The heat flux is directed from the metal (podłoże) to the coating. The test method provides accelerated conditions for cathodic stripping that occurs under simulated heating and provides a measurement of the resistance of the coating to such effects.

4.2 The effect of the test will be evaluated by physical examination and monitoring the current consumed by the test sample. Usually there is no correlation between the two evaluation methods, but both are significant. The physical examination involves assessing the effective contact of the coating with the metal surface based on the observed difference in relative adhesive bonding. It is often found that the cathodic debonding region propagates from the region where adhesion is zero to the region where adhesion has reached the original level. There may also be intermediate areas of reduced adhesion.

4.3 Założenia związane z wynikami testów obejmują:

ASTM D 6676-2021 “Oznaczanie złuszczalności katodowej powłok ścian rur po nagrzaniu metodą ogrzewania wewnętrznego”

4.3.1 The maximum adhesion or bonding force is found in the coating not immersed in the test liquid, I

4.3.2 The reduced adhesion in the immersion test area is the result of cathode debonding.

4.4 On a comparative basis, the ability to resist stripping is of professional quality, but stripping in this test method is not necessarily an unfavourable indication of coating performance. The advantage of this test method is that all the dielectric type coatings that are now commonly used destick to some extent, umożliwiając w ten sposób porównanie jednej powłoki z drugą.

4.5 The current flow in the test unit is a relative indicator of the extent of the area requiring corrosion protection; Jednakże, gęstości prądu występujące w tym teście są znacznie większe niż normalnie wymagane do ochrony katod w naturalnym środowisku gruntu śródlądowego.

4.6 Test voltages higher than the recommended voltage may cause chlorine gas formation. Subsequent chemical effects on the coating may call into question the interpretation of the test results. A filter tube with a sintered disk (see test method G95) or a sand layer (40 siatka) on the coated surface can reduce this effect.

ASTM D 6676-2021 “Oznaczanie złuszczalności katodowej powłok ścian rur po nagrzaniu metodą ogrzewania wewnętrznego”

Zakres
1.1 This test method describes an accelerated procedure for determining the comparative characteristics of a coating system applied to the exterior of a steel pipe to prevent or mitigate corrosion that may occur underground or in water where the pipe carries a heating medium and is under cathodic protection. The test method is intended for use on samples of coated tubes, or specimens cut from coated tubes or plate parts, and is applicable to such samples when the coating has an electrical barrier function.

1.2 The test method is designed to simulate the exposure of the outer coating to the high temperature inside the pipe and the ambient temperature outside, thus being affected by the temperature gradient. If high temperature is required but no temperature gradient is available, see Test Method G42.

1.3 Values expressed in SI units or inch-pound units should be treated separately as standard values. Wartości określone w każdym systemie nie muszą być takie same; Dlatego, aby zapewnić zgodność z normami, każdy system powinien być używany niezależnie od siebie i nie należy łączyć wartości obu systemów.

ASTM D 6676-2021 “Oznaczanie złuszczalności katodowej powłok ścian rur po nagrzaniu metodą ogrzewania wewnętrznego”

1.4 Celem tej normy nie jest omówienie wszystkich kwestii związanych z bezpieczeństwem, Jeśli w ogóle, związane z jego użytkowaniem. Obowiązkiem użytkownika niniejszej normy jest zapewnienie odpowiedniego bezpieczeństwa, praktyk zdrowotnych i środowiskowych oraz w celu określenia możliwości zastosowania ograniczeń regulacyjnych przed użyciem.

1.5 Niniejsza norma międzynarodowa została opracowana zgodnie z uznanymi na arenie międzynarodowej zasadami normalizacji, ustanowionymi w Decyzji w sprawie zasad opracowywania norm międzynarodowych, Wytyczne i zalecenia wydane przez Komitet ds. Barier Technicznych w Handlu Światowej Organizacji Handlu.