Semnificație și scop
4.1 The test method measures the degree to which the sharp corners are covered by different coating powder materials. Corner coverage is affected by surface thickness, thixotropy, melt viscosity, surface tension, curing rate, and application and curing temperature.

Scopul
1.1 The test method consists of determining the ratio of angular thickness (vedea 3.1.3) to face thickness (vedea 3.1.4) of a powder coating applied to a specific face thickness by immersing a preheated square rod in an aerated powder and curing the coating with predetermined conditions.

ASTM D 2967-2017 “Acoperirea colțului de acoperire cu pulbere”

Notă 1: The property of corner coverage is also known as “edge coverage”, but the latter is not recommended. There are widespread misconceptions and expectations about the term “edge coverage”. The test was performed on rebar with square angles and the results are not necessarily associated with sharper edges, namely burrs. Coatings with measurable corner coverage may still not protect sharper edges from corrosion or provide the electrical insulation required for some applications.

1.2 Valorile exprimate în unități SI vor fi considerate standarde. Valorile date în paranteze sunt doar pentru referință.

1.3 Acest standard nu este destinat să abordeze toate problemele de siguranță, dacă există, asociat cu utilizarea acestuia. Este responsabilitatea utilizatorilor acestui standard de a stabili practici adecvate de securitate și sănătate și de a determina aplicabilitatea restricțiilor de reglementare înainte de utilizare..

1.4 Acest standard internațional a fost elaborat în conformitate cu principiile de standardizare recunoscute la nivel internațional stabilite în Decizia privind principiile pentru elaborarea standardelor internaționale., Orientări și recomandări emise de Comitetul pentru bariere tehnice în calea comerțului al Organizației Mondiale a Comerțului.