ASTM B530 วิธีทดสอบมาตรฐานสำหรับการวัดความหนาของผิวเคลือบทางแม่เหล็ก: Electrodeposited Nickel Coatings on Magnetic and non-magnetic Substrates includes non-destructive measurement of the thickness of electrodeposited nickel coatings on magnetic or non-magnetic substrates using a magnetic instrument.
ความหมายและการใช้งาน

5.1 โดยทั่วไปความหนาของสารเคลือบมีความสำคัญต่อประสิทธิภาพ. This magnetic method is suitable for non-destructive measurement of thickness and specification acceptance of certain nickel coatings.

5.2 The method requires that the magnetic properties of the coating and its substrate be the same as those of the reference standard used for instrument calibration adjustment.

5.3 The method should not be used to determine the thickness of self-catalyzed deposited nickel-phosphorus alloys containing more than 8% P in steel. As long as the measurements are made prior to any heat treatment, those coatings are sufficiently non-magnetic for test method B499 to be suitable for the determination.

B530-2014 “วิธีทดสอบมาตรฐานสำหรับการวัดความหนาของผิวเคลือบด้วยวิธีแม่เหล็ก: การเคลือบนิกเกิลด้วยไฟฟ้าบนพื้นผิวแม่เหล็กและไม่ใช่แม่เหล็ก”

ขั้นตอน 1: ขอบเขต

1.1 This test method includes non-destructive measurement of the thickness of an electrodeposited nickel coating on a magnetic or non-magnetic substrate using a magnetic instrument. It is intended to complement the manufacturer’s instructions on the operation of the instrument, ไม่ใช่เพื่อแทนที่พวกเขา.

1.2 These instruments measure the magnetic attraction between the magnet and the coating – substrate combination (classified as “magnetic pull-off”), or the change in magnetic flux density within the probe (classified as “electron”).

1.3 For this test method, two types of coating-substrate combinations can be encountered: ประเภท ก, nickel coatings on magnetic substrates, and Type B nickel coatings on non-magnetic substrates.

1.4 The effective measurement range of instruments using the magnetic attraction principle is up to 50μm (2 ล้าน) for type A coatings and up to 25μm (1 ล้าน) for type B coatings. For gauges based on the principle of flux density variation, the effective range is much larger and measurements up to 1 มม (40 ล้าน) or higher can be made on both types of coatings.

1.5 Measurements made in accordance with this test method shall comply with the requirements of ISO Standard 2361, printed in 1982.

1.6 ค่าที่แสดงเป็นหน่วย SI ถือเป็นค่ามาตรฐาน. ค่าที่ระบุในวงเล็บมีไว้เพื่อการอ้างอิงเท่านั้น.

1.7 มาตรฐานนี้ไม่ได้มีวัตถุประสงค์เพื่อจัดการกับข้อกังวลด้านความปลอดภัยทั้งหมด, ถ้ามี, ที่เกี่ยวข้องกับการใช้งาน. เป็นความรับผิดชอบของผู้ใช้มาตรฐานนี้ในการกำหนดแนวทางปฏิบัติด้านความปลอดภัยและสุขภาพที่เหมาะสม และเพื่อพิจารณาการบังคับใช้ข้อจำกัดด้านกฎระเบียบก่อนใช้งาน.