Betekenis en doel
4.1 The test method measures the degree to which the sharp corners are covered by different coating powder materials. Corner coverage is affected by surface thickness, thixotropy, melt viscosity, surface tension, curing rate, and application and curing temperature.

Reikwijdte van
1.1 The test method consists of determining the ratio of angular thickness (zien 3.1.3) to face thickness (zien 3.1.4) of a powder coating applied to a specific face thickness by immersing a preheated square rod in an aerated powder and curing the coating with predetermined conditions.

ASTM D 2967-2017 “Hoekcoating van poedercoatings”

Opmerking 1: The property of corner coverage is also known as “edge coverage”, but the latter is not recommended. There are widespread misconceptions and expectations about the term “edge coverage”. The test was performed on rebar with square angles and the results are not necessarily associated with sharper edges, namely burrs. Coatings with measurable corner coverage may still not protect sharper edges from corrosion or provide the electrical insulation required for some applications.

1.2 Waarden uitgedrukt in SI-eenheden worden als normen beschouwd. De waarden tussen haakjes zijn alleen ter referentie.

1.3 Deze norm is niet bedoeld om alle veiligheidsproblemen aan te pakken, indien aanwezig, die verband houden met het gebruik ervan. Het is de verantwoordelijkheid van gebruikers van deze norm om passende veiligheids- en gezondheidspraktijken vast te stellen en voorafgaand aan gebruik de toepasbaarheid van wettelijke beperkingen te bepalen..

1.4 Deze internationale norm is ontwikkeld in overeenstemming met de internationaal erkende standaardisatieprincipes die zijn vastgelegd in het Besluit over de beginselen voor de ontwikkeling van internationale normen, Richtlijnen en aanbevelingen uitgegeven door het Comité voor technische handelsbelemmeringen van de Wereldhandelsorganisatie.