4.1 I rivestimenti con prestazioni soddisfacenti devono aderire al substrato su cui sono applicati. It has been found that the test method can be used to distinguish the degree of adhesion of the coating to the substrate. It is most applicable to provide a relative rating for a range of coated plates that exhibit significant differences in adhesion.

4.2 Studies conducted in the laboratory using the ring pen specified in the previous edition have shown that meaningful adhesion data are not possible when a load of 10 A 20 kg is required to break the surface of the solvent-based coating. When a load of this magnitude is required, the chrome-plated ring stylus vibrates and jumps on the coated surface. Similar meaningless data were obtained when testing required more than 10kg of powder paint to destroy the surface. Perciò, testing under these conditions is not applicable.

ASTM D2197-16-2022 Valutazione dell'adesione di rivestimenti organici mediante metodo Scratch

Ambito di applicazione

1.1 This test method covers the determination of adhesion of organic coatings such as paint, varnish and lacquer on smooth, Piatto (Piatto) panel surfaces.

1.2 Values expressed in SI units are treated as standards. I valori indicati tra parentesi sono solo di riferimento.

1.3 Questo standard non è destinato ad affrontare tutti i problemi di sicurezza, se presente, legati al suo utilizzo. È responsabilità degli utenti di questo standard stabilire una sicurezza adeguata, pratiche sanitarie e ambientali e per determinare l'applicabilità delle restrizioni normative prima dell'uso.

1.4 La presente norma internazionale è stata sviluppata in conformità con i principi di standardizzazione accettati a livello internazionale stabiliti nelle decisioni del Comitato sugli ostacoli tecnici agli scambi (TBT) dell’Organizzazione Mondiale del Commercio sulla formulazione di norme internazionali, linee guida e principi raccomandati.